Abstract:The novel Bi-substituted rare-earth iron garnet films were grown by the modified liquid phase epitaxy (LPE) technique for use as a 45° Faraday rotator in optical isolators. First, single crystals of Y3Fe5O12 (YIG), with a lattice constant of 1.2378 nm, were grown by means of the Czochralski method. Using the seed crystal of YIG instead of the conventional non-magnetic garnet of Gd3Ga5O12 as a substrate, a film of BiYbIG was grown by means of the LPE method from Bi2O3–B2O3 fluxes. The structural, magnetic and magneto-optical properties of BiYbIG LPE film/YIG crystal composite have been investigated using directional X-ray diffraction, electron probe microanalysis, vibrating sample magnetometer and near-infrared transmission spectrometry. The saturation magnetization 4πMs has been estimated to be approximately 1200 G. The Faraday rotation spectrum was measured by the method of rotating analyzer ellipsometry with the wavelength varying from 800 to 1700 nm. The resultant Bi0.37Yb2.63Fe5O12 LPE film/YIG crystal composite showed an increased Faraday rotation coefficient due to doping Bi3+ ions on the dodecahedral sites of the magnetic garnet without increasing absorption loss, therefore a good magneto-optic figure of merit, defined by the ratio of Faraday rotation and optical absorption loss, has been achieved of 21.5 deg/dB and 30.2 deg/dB at 1300 nm and 1550 nm wavelengths, respectively, at room temperature. Since Yb3+ ions and Y3+ ions provide the opposite contributes to the wideband and temperature characteristic of Faraday rotation, the values of Faraday rotation wavelength and temperature coefficients were reduced to 0.06%/nm and 0.007 deg/°C at 1550 nm wavelength, respectively.

On the growth and magneto-optical properties of (YbTbBi)3Fe5O12 bulk single crystal

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

Temperature-stable Faraday rotation TbYbBiIG single crystals and magneto-optical properties

Study on wideband and temperature properties of TbybBiIg crystal in 1500 similar to 1620nm band

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

GROWTH AND MAGNETO-OPTICAL PROPERTIES IN OPTICAL COMMUNICATION BAND FOR(TbBi)_3Ga_XFe_(5-x)O_(12) FILM/ (tbybbi)_3fe_5o_(12) CRYSTAL COMPOSITE STRUCTURE

The Growth And Magneto-Optical Properties Of Large Size Single-Crystal Thick Tmbiig Films From Lead-Free Flux By Lpe Technology

The Origin of Enhanced Magnetodielectric Effect in Y3-xYbxFe5O12 Ceramics

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

Magnetostriction Increase of Tb0.3dy0.7fe1.95 Alloy Prepared by Solidification in High Magnetic Fields

Multiferroic Properties of Y-doped BiFeO3

Faraday Rotation Spectra Analysis Of Bi-Substituted Mixed Rare-Earth Iron Garnet Crystals In Optical Communication Band

Liquid phase epitaxy growth of bismuth-substituted yttrium iron garnet thin films for magneto-optical applications

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

CRYSTAL GROWTH OF Y<sub>3-x</sub>Bi<sub>x</sub>Fe<sub>5</sub>O<sub>12</sub>

Growth, optical dispersion and magnetic behavior of Dy3+ doped yttrium iron garnet crystals

Transparent non-stoichiometric Tb2.45Hf2O7.68 magneto-optical ceramics with high Verdet constant

Magnetostriction of Tb0.36Dy0.64(Fe1−xCox)2 (x=0–0.20) 〈112〉-oriented crystals

Morphology evolution and enhanced magnetostriction of (Fe<sub>0.81</sub>Ga<sub>0.19</sub>)<sub>99.9</sub>Tb<sub>0.1</sub> crystals prepared by liquid metal cooling Bridgman directional solidification

Growth and magneto-optical properties of Bi25FeO40 crystals with heavy Co/Fe co-doping