Energy transfer process of Nd3+/Ho3+ co-doped fluoride halide glasses with anion substituted multi-wavelength tunable mid-infrared luminescence
Hao Yin,Xiaosong Zhang,Lan Li,Jiajia Zhang,Zhaowei Zhang,Xin Liu,Xiaokai Gong,Rukun Ding
DOI: https://doi.org/10.1016/j.jre.2020.10.004
IF: 4.632
2021-11-01
Journal of Rare Earths
Abstract:Ho3+ doped ZBLAN glass with 2.0 and 2.9 μm emission was prepared. In order to further improve the luminescence of Ho3+, halogen ions (Cl, Br, I) were introduced to reduce the maximum phonon energy and phonon state density of the sample. At the same time, Nd3+ was introduced to transfer the energy to Ho3+ pumped with a 793 nm laser (Nd3+:4F5/2,4F3/2→Ho3+:5I6). The effect of different halogen ion on the luminescent properties of the fluoride halide glass was compared. The results show that the luminescent intensity of infrared increases with the introduction of different halogen ions. By comparison, it is found that the sample with I– has the strongest luminescence of 1064 nm, 2.0 μm and 2.9 μm. This is consistent with the calculated J-O intensity parameters. In addition, the 2.0 and 2.9 μm emission of Ho3+ pumped with a 450 nm laser will not disappear. A mid-infrared sample with multi-wavelength excitation and multi-wavelength emission can be obtained. Nd3+/Ho3+ co-doped fluoride halide glasses with 1064 nm, 2.0 μm and 2.9 μm luminescence were prepared by melt quenching method. The luminescent mechanism and the energy transfer process between the two ions of Nd3+/Ho3+ co-doped fluoride halide glass were studied. The J-O parameters, luminescence lifetime and absorption emission cross-sectional area of Ho3+ and Nd3+ were calculated, respectively. It is found that the value of Ω 2 in the glass matrix increases with the introduction of different halogen ions, while Ω 4 and Ω 6 do not change obviously in different glass compositions. This is because the environment of the crystal field around the rare earth ions changes. The crystal phase and phonon energy of the sample were analyzed by X-ray diffraction pattern and a Fourier transform infrared spectrometer, respectively. Based on the above spectra and data (phonon energy is 634.71 cm−1), it can be predicted that Nd3+/Ho3+ co-doped fluoride halide glass is a potential mid-infrared luminescent material.
chemistry, applied