Abstract:A series of compounds with the ${\mathrm{ThMn}}_{12}$-type structure, R${\mathrm{Fe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ (R=Y, Sm, Gd, Tb, Dy, Ho, Er, and Lu), were synthesized. The corresponding nitrides, obtained by gas-solid reactions, retained the same structure as their parent compounds, but with a relative volume expansion of 3%. The Nb atoms occupy the 8i sites in the ${\mathrm{ThMn}}_{12}$ structure. The highest Curie temperatures are 597 K and 773 K for ${\mathrm{GdFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ and its nitride, respectively. The average iron magnetic moment ${\mathrm{\ensuremath{\mu}}}_{\mathrm{Fe}}$ at T=1.5 K is 1.9${\mathrm{\ensuremath{\mu}}}_{\mathit{B}}$ for parent compounds and 2.1${\mathrm{\ensuremath{\mu}}}_{\mathit{B}}$ for the nitrides. By the introduction of nitrogen, the Fe-Fe exchange interaction is much strengthened while the R-Fe exchange interaction is slightly weakened. The enhancement of ${\mathrm{\ensuremath{\mu}}}_{\mathrm{Fe}}$ by the influence of interstitial nitrogen is about 11%. The Fe sublattices of R${\mathrm{Fe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ compounds and their nitrides have an easy c-axis anisotropy. At T=1.5 K, the anisotropy constant ${\mathit{K}}_{1}$(Fe) is 25.7 K/f.u. for the parent compounds and 21.9 K/f.u. for the nitrides. The reduction of ${\mathit{K}}_{1}$(Fe) by the influence of interstitial nitrogen is about 17%. Spin-reorientation transitions were observed in ${\mathrm{DyFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ and ${\mathrm{ErFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ compounds. The complex magnetic behavior of R${\mathrm{Fe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ at low temperatures can be explained by exchange and crystal-field-interaction models. The ${\mathrm{SmFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ compound has an anisotropy field of 10.0 T at room temperature. Its high Curie temperature and magnetization make it a potential candidate for applications as a permanent magnet.

Variation Of Magnetic-Properties As A Function Of Mo Content In The Rfe(12-X)Mo(X) Series And Their Nitrides (R=Y, Nd, Gd)

Magnetic Properties Of Rfe10.5mo1.5cx And Their Nitrides

Magnetic-Properties of New Series R-Mo-Fe Nitrides with the Thmn12-Type Structure at A Lower Mo Content

Magnetic phase transitions and magnetic properties of nd3(fe, mo)29 compound and its nitride

Crystallographic and Magnetic Properties of R3Fe29-xTx and Their Nitrides, Carbides and Hydrides

Structual and Magnetic Properties of RMo1.5Fe10.5Nx

Crystallographic and Intrinsic Magnetic Properties of Nd1−xDyxFe10.5Mo1.5 Compounds and Their Nitrides (X=0.0−1.0)

Magnetic Properties of Nd(Fe1-xCox)10.5M1.5 (m=mo and V) and Their Nitrides

Study Of The Magnetocrystalline Anisotropy Of Yfe(12-X)Mo(X) And Yfe(12-X)Mo(X)N(Y) (X=1-3, Y-Similar-Or-Equal-To-1)

STRUCTURAL CHARACTERIZATION AND INTRINSIC MAGNETIC PROPERTIES OF THE R3 (Fe,Mo)29 NITRIDES

Magnetic properties and magnetic domain structures of NdFe10.5Mo1.5 and NdFe10.5Mo1.5Nx

Phase Transformation and Magnetic Properties of Mechanically Alloyed Ndfe12-Xmoxny

Structure and magnetic properties of Y(Fe1−xMnx)12 compounds and their nitrides (x = 0.2 and 0.4)

Study on neutron diffraction and correlated magnetic properties of (R1−xZrx)Fe12−yMoy with low Mo concentration

STUDY ON THE STRUCTURAL AND MAGNETIC PROPERTIES OF RFe10.5V1.5Nx

Structure and magnetic phase diagram of mixed rare-earth Nd1−xTbxFe10.5Mo1.5 compounds

Magnetic-Properties of Prfe12-Xmox and Prfe12-Xmoxny (X=1-2.5)

Structure And Magnetic-Properties Of Rfe(11.35)Nb(0.65) And Rfe(11.35)Nb(0.65)N(Y) (R=Y, Sm, Gd, Tb, Dy, Ho, Er, And Lu)

Influence on magnetic properties of substitution of Ni for Fe in GdFe11.3Nb0.7 compound

Structural and Magnetic Properties of (ndxr1−x)3fe24cr5 (r=gd and Tb) Intermetallic Compounds

Formation, Structure and Magnetic Properties of TbFe12−xMox (x=0.5–3.0) Compounds