Crystal Growth, Polarization Spectral Analysis Derived from the Broadband Emission from the 1D2 Level of Pr:GdScO3 Crystal
Wudi Wang,Jie Tian,Na Li,Jian Liu,Donghua Hu,Jianshu Dong,Hui Lin,Qingguo Wang,Yanyan Xue,Xiaodong Xu,Dongzhen Li,Zhanshan Wang,Jun Xu
DOI: https://doi.org/10.1364/ome.443715
2022-01-01
Optical Materials Express
Abstract:Pr3+-doped GdScO3 single crystal was successfully grown by the Czochralski (Cz) method. Polarized absorption spectra, polarized fluorescence spectra, and fluorescence decay curves were measured at room temperature. The polarized spectroscopic property of Pr:GdScO3 crystal for new-wavelength transition in the near infrared (NIR) region was discussed for the first time. The absorption cross-sections at 600 nm were calculated to be 0.39×10−20 cm2 (E∥a), 0.32×10−20 cm2 (E∥b) and 0.4×10−20 cm2 (E∥c). The emission cross sections at 1053 nm of 1D2 energy level were calculated to be 0.86×10−20 cm2 (E∥a), 0.79×10−20 cm2 (E∥b) and 0.78×10−20 cm2 (E∥c), with FWHM of 57.54 nm, 57.96 nm and 58.96 nm, respectively. The fluorescence lifetime and radiative lifetime of the 1D2 energy levels of Pr3+ ions were 45.46 µs and 393.94 µs, respectively. Those results show that the Pr:GdScO3 crystal should be the potential near infrared laser gain medium originated from the 1D2 transition.