Abstract:The effect of sintering atmosphere (air and Ar) and temperature (1100, 1200, 1300 °C) on the microstructure, mechanical properties, and bioactivity of hydroxyapatite/tantalum (HA/Ta) composites were systematically investigated by pressureless sintering of the mixture of HA and Ta powders. It shows that the sintering atmosphere greatly impacts the phase composition and microstructure of the HA/Ta composites. The higher diffusion of atoms promotes shrinkage and causes deeper reaction fusion between the HA matrix and Ta, which improved the interfacial binding of the HA/Ta composites. The refined grain structure and improved interfacial binding obtained within the Ar atmosphere compared to the air atmosphere benefit the mechanical properties. The maximum bending strength and shrinkage observed for the composites sintered at 1300 °C in the Ar atmosphere are 27.24 MPa and 6.65%, respectively. The cell counting kit-8 (CCK-8) method was used to investigate the in vitro cytocompatibility of HA/Ta composites. The results revealed that the HA/Ta composites sintered with different conditions have no cytotoxicity. The simulated body fluid (SBF) soaking results showed that all of the studied composites possess desirable bioactivity, as demonstrated by their ability to form calcium-deficient carbonate apatite layer on the surfaces. For composites sintered at 1300 °C, the surface apatite layer coverage of the composites obtained in the Ar atmosphere was increased by 139.7% than the ones obtained in air, which confirmed an enhanced bioactive mineralization ability. The results indicated that the HA/Ta composites sintered at 1300 °C in Ar possess desirable mechanical properties and bioactivity. This work opens up the new possibility for preparing HA-based composites and is of great value in biomedical applications.This article has not yet been cited by other publications.

Effect of iron on the sinterability and properties of HA/Ti-Fe composites

Toughening mechanisms in iron-containing hydroxyapatite/titanium composites

Hydroxyapatite Reinforced With Ti-Fe Particle: Correlation Between Composition, Microstructure And Mechanical Properties

Microstructure and mechanical properties of iron-containing titanium metal-metal composites

Study of the Mechanical Property of Magnetite/ Hydroxyapatite/ Chitosan Nano-Composite

Sintering test research with addition of hematite concentrate

Effect of Fe addition on properties of Ti-6Al-xFe manufactured by blended elemental process

Fabrication of Hydroxyapatite/Tantalum Composites by Pressureless Sintering in Different Atmosphere

Influence of ferrous iron incorporation on the structure of hydroxyapatite

Simultaneously improving the strength and ductility of the as-sintered (TiB+La2O3)/Ti composites by in-situ planting ultra-fine networks into the composite powder

Effect of Fe content on microstructure and hardness of Ti-4.5Mo–5Al-1.8Zr-2.5Cr-1.1Sn titanium alloy based on high-throughput diffusion couple

Densification, Microstructure and Mechanical Performance of TiC/Fe Composites by Spark Plasma Sintering

Microstructure and mechanical properties of powder metallurgy Ti-TiBw-xFe titanium matrix composites using Ti-TiBw composite powder

Formation mechanism of interdiffusion layer and mechanical properties of Al 0.6 CoCrFeNi high-entropy alloy/Ti composites

Enhancing strength-ductility synergy in nano-sized TiB 2 /Al composite via rapid solidification and thermo-mechanical processing

Effect of TiC addition on the microstructure and mechanical properties of FeCoCrNiMn high entropy alloy fabricated by selective laser melting

Microstructure, Mechanical Properties, and Sintering Behavior of Ti3O-Fe2TiO4-TiC Composites

Effect of sintering temperature on the microstructure and properties of Ti/W–C reinforced Fe-based composites

Enhanced anticorrosion and tribological properties of Ti6Al4V alloys with Fe3O4/HA coatings

Investigating phase transformation, densification and diffusion mechanism of TiH 2 powder to achieve a high ductile Ti6Al4V alloy

Microstructure and mechanical properties of tungsten fiber reinforced tungsten composites prepared by Fe activated sintering