Abstract:Rare earth (RE) elements have large solid solubility in magnesium and are widely used to regulate the microstructure and property of advanced magnesium alloys. However, different kinds of RE elements have different effects on microstructure and property of the alloy. In this study, a Mg–Zn–Y alloy and a Mg–Zn–Gd alloy with alloying elements of the same atomic percentage were designed to clarify the effect of yttrium (Y) and gadolinium (Gd) on the corrosion behavior of as-cast MgZn 2 Y 2.66 and MgZn 2 Gd 2.66 alloys. The results show that the MgZn 2 Y 2.66 alloy is mainly composed of α-Mg phase and long period stacking ordered (LPSO) phase, while MgZn 2 Gd 2.66 alloy is mainly composed of α-Mg phase and (Mg, Gd) 3 Zn phase (W phase). Generally speaking, the corrosion phenomena of the two alloys in 3.5 wt% NaCl solution are similar. In the early stages of exposure, the alloys underwent uniform corrosion at a relatively low corrosion rate. With prolonged exposure, localized corrosion became dominated and the corrosion rate was greatly increased. However, the corrosion rate of the MgZn 2 Y 2.66 alloy, in terms of the corrosion current density, is about one order of magnitude lower than that of the MgZn 2 Gd 2.66 alloy. The high corrosion resistance of the MgZn 2 Y 2.66 alloy is mainly attributed to the presence of LPSO phase in form of continuous networks and the relatively high corrosion resistance of the corrosion product layer on the alloy.

Corrosion Behaviors of Mg-7Gd-5Y-1Nd-0.5Zr Alloys in CO<sub>2</sub> Atmosphere under Different Relative Humidity

Corrosion Behaviors for Peak-Aged Mg–7Gd–5Y–1Nd–0.5Zr Alloys with Oxide Films

The Corrosion Behaviors of Mg–7Gd–5Y–1Nd–0.5Zr Alloy under (NH4)2SO4, NaCl and Ca(NO3)2 Salts Spray Condition

Investigation of Corrosion Behaviors of Mg–6Gd–3Y–0.4Zr Alloy in NaCl Aqueous Solutions

Effect of grain size and crystal orientation on the corrosion behavior of as-extruded Mg-6Gd-2Y-0.2Zr alloy

Corrosion Mechanism of Mechanically Alloyed Mg50ni50 and Mg45cu5ni50 Alloys

Comparison of the Corrosion Behaviors of Mg–Gd–Y–Zn–Zr Alloys Fabricated by Different Preparation Methods

Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg–Zn–Y and Mg–Zn–Gd Alloys

Effect of SO2 and NH3 on the Corrosion Failure of Zn-Al-Mg Coatings

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Corrosion Behavior of Extrusion, Under-Aged, Peaked-Aged and Over-Aged We93 Alloys in Nahso3 Solutions

Comparative Study on Corrosion Behavior of As-Cast and Extruded Mg–5Y–7Gd–1Nd–0.5Zr Alloy in 5% NaCl Aqueous Solution

Effect of Mo Addition on Corrosion Behavior of High-Entropy Alloys CoCrFeNiMox in Aqueous Environments

Corrosion Behaviour of Ni-based Alloys 230, 617, and 601 in CO2 Gas at 750 and 850°C

Effect of water vapor content on the corrosion mechanism of HR3C in simulated oxy-coal combustion environment

Recent Progress on Atmospheric Corrosion of Field-Exposed Magnesium Alloys

Investigation on the Corrosion Behavior of Cast and Extrude AZ61 Mg Alloys in NaCl Atmosphere at High Temperature and Pressure

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

The Corrosion Behavior of AZ91D Magnesium Alloy in Simulated Haze Aqueous Solution

Corrosion behavior characterization of as extruded Mg-8Li-3Al alloy with minor alloying elements (Gd, Sn and Cu) by scanning Kelvin probe force microscopy

Corrosion Behavior and Mechanical Performance of 7085 Aluminum Alloy in a Humid and Hot Marine Atmosphere