Abstract:Abstract Rebar is an important material in the major structural engineering, and its fine structure has a very important effect on the performance of the rebar. In this work, the Gleeble-3800 thermal simulator was used to simulate and control the final cooling temperature process to explore the effect of the precipitation behavior of the microalloying elements on the microstructure and mechanical properties of the rebar. The electron backscatter diffraction (EBSD), high-resolution transmission electron microscope (TEM), and universal tensile testing machine were used to characterize the microstructural transformation and mechanical properties of high-strength anti-seismic rebar. The results shows that under the conditions of different final cooling temperatures, the microstructure of the rebar were mainly composed of ferrite and pearlite. When the final cooling temperature decreased from 750 °C to 650 °C, the ferrite grain size decreased from 0.01237 mm to 0.00678 mm and the pearlite lamellar spacing decreased from 0.226 μ m to 0.114 μ m. The EBSD results found that the most of ferrite grains with larger misorientation angle (20° ∼ 60°) formed by the different austenite grains. The TEM results found that the main precipitates were (Nb, Ti, V) C, which precipitated on the ferrite matrix, and the shapes were oval, and the average particle sizes were about 20 ∼ 30 nm. When the final cooling temperature was 650 °C, the tensile strength and yield strength of the rebar reached 712.94 MPa and 562.97 MPa, respectively, and strength yield ratio was 1.27. With the decreases in the final cooling temperature, the tensile strength and yield strength of the rebar gradually increased.

Research on Secondary Cooling Technology for Billet of HRB500E Vanadium-Containing Steel Rebar

Study on Billet Temperature Prediction and Furnace Temperature Optimal Setting of Regenerative Reheating Furnace

Study on CCT Curve and Microstructure Evolution of HRB500E

Effect of High Temperature Exposure and Strain Rate on Mechanical Properties of High-Strength Steel Rebars

Study on CCT Curve and Microstructure Evolution of a Vanadium-Containing Steel Rebar

Hot Ductility Behaviors of HRB600 Vanadium-Containing Steel Rebar

Effects of controlled cooling temperature on microstructure and peformance of V-Nb microalloyed high-strength rebars

Research and development practice of HRB400 hot rolled ribbed steel bar

Effect of final cooling temperature on the microstructure and mechanical properties of high-strength anti-seismic rebar

Research on Low-Cost Vanadium Alloying in Producing Vanadium-Containing Seismic Resistant Rebar

Development of Air-Cooled Super Strength Finish Rolled Rebar

500Mpa Seismic Rebars Developed by Nitrogen-Rich and Vanadium-Microalloyed, Controlled Cooling Technology

Secondary Cooling Design for Slab Caster Based on Transient Heat Transfer Module

Design and implementation of an automated secondary cooling system for the continuous casting of billets

Effects of Different Microalloying and Controlled Cooling Technology on Microstructure and Properties of 500mpa High-Strength Rebars

Simulation of Subrapid Solidification and Secondary Cooling for the Strip Casting of IF Steel

Temperature Influence on Section Uniformity of Casting Steel Rolled with the Hot-Core Heavy Reduction Rolling Process and Traditional Hot Rolling Process

Laboratory Experimental Setup And Research On Heat Transfer Characteristics During Secondary Cooling In Continuous Casting

Strengthening mechanism of HRB400 rebar bearing chromium or vanadium

Effect of Reheating Temperature on Continuous Cooling Transformation, Microstructure and Properties of Nb Microalloyed Rebar

Effect of Cooling Rate after Deformation on Microstructure of V-N Microalloying High Strength Aseismic Rebar