Improved magnetic properties of SrFe12O19/FeCo core-shell nanofibers by hard/soft magnetic exchange-coupling effect

Juan Dong,Yi Zhang,Xinlei Zhang,Qingfang Liu,Jianbo Wang

DOI: https://doi.org/10.1016/j.matlet.2014.01.022

IF: 3

2014-01-01

Materials Letters

Abstract:Hard/soft SrFe12O19/FeCo composite nanofibers with core–shell structure have been synthesized by reduction process in a hydrogen atmosphere. As the precursor, SrFe12O19/CoFe2O4 core–shell nanofibers were prepared by coaxial electrospinning and calcination process. SrFe12O19/CoFe2O4 composite ferrites were formed after calcined at 900°C for 1h. The core–shell nanofibers show an enhanced saturation magnetization (Ms) of 60.9emu/g for SrFe12O19/CoFe2O4 and 68.8emu/g for SrFe12O19/FeCo comparing with SrFe12O19 nanofibers (53.4emu/g). The coercivities (Hc) for SrFe12O19/CoFe2O4 and SrFe12O19/FeCo core–shell nanofibers decrease to 3190Oe and 1249Oe, respectively. The hysteresis loop for SrFe12O19/FeCo core–shell nanofibers shows a single-phase magnetization behavior. The improvement in magnetic properties for core–shell structure composite nanofibers is attributed to the exchange–coupling interaction between the hard and soft phases.