Improved magnetic performance at low and high temperatures in non-exchange-coupling CoFe 2 O 4 /CoFe 2 nanocomposites

xiaoming sun,y q ma,y f xu,s t xu,b q geng,z x dai,g h zheng

DOI: https://doi.org/10.1016/j.jallcom.2015.05.009

IF: 6.2

2015-01-01

Journal of Alloys and Compounds

Abstract:Numerous efforts were made to improve the magnetic performance of the CoFe2O4 (hard)/CoFe2 (soft) composite. Unfortunately almost all reported Mr/Ms values are smaller than 0.5. Based on the analyses of our previous work and the results in literature reported by other groups, it can be suggested that the severely agglomerated nanoparticles result in the strong interparticle dipolar interaction, which suppresses the Mr/Ms ratio. In this work the dispersive and uniform CoFe2O4 nanoparticles were synthesized, as shown in the inset of figure (a), and subsequently reduced in H2 ambient for 90, 240 and 480min to obtain the CoFe2O4/CoFe2 composites. The reduction reaction was performed at relatively low temperature of 300°C in order to weaken as possibly the aggregating degree.