Separated CoFe2O4/CoFe Nanoparticles by the SiO X Matrix: Revealing the Intrinsic Origin for the Small Remanence Magnetization

B. Q. Geng,Y. Q. Ma,Y. F. Xu,S. T. Xu,X. Sun,G. H. Zheng,Z. X. Dai

DOI: https://doi.org/10.1007/s11051-015-3087-1

IF: 2.533

2015-01-01

Journal of Nanoparticle Research

Abstract:In order to clarify the intrinsic reason for the smaller remanence (M r)-to-saturation (M s) magnetization ratio M r/M s than that expected by the Stoner–Wohlfarth model in CoFe2O4/CoFe2 nanoparticles in the previous report, we first prepared well-dispersed CoFe2O4 nanoparticles, and then they were diluted in the SiO2 matrix followed by reduction in H2 as far as possible to exclude or reduce disadvantageous variables (such as the growth and aggregation of particles and the exchange coupling between soft magnetic particles in the process of reducing) affecting magnetic properties. Such an idea has not been taken into account before to our knowledge. The analyses on the magnetic results indicate that the CoFe2O4/CoFe2 nanoparticles herein reported are a pure dipolar system, in which the coercivity (H c) and M r/M s ratio are very sensitive to the anisotropy and the strength of dipolar interaction. These results signify that it is important to maintain the CoFe2O4/CoFe2 nanoparticles with higher anisotropy and weaker dipolar interaction for improving M r/M s and H c. This suggestion was further confirmed by our another result wherein an M r/M s value of 0.64 was obtained even though no exchange coupling was observed in the CoFe2O4/CoFe2 nanoparticles, and further work is in process.