Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Failure Behavior Investigation of a Unidirectional Carbon–carbon Composite

Compressive testing and failure analysis of three-dimensionally reinforced carbon/carbon composites

Failure behavior and damage visualization of thick carbon/aramid hybrid woven composites under flexural loading conditions

Compressive properties and failure mechanism of 3D C/C composites

The failure mechanism of carbon fiber-reinforced composites under longitudinal compression considering the interface

Failure Modes and Toughening Mechanisms in CMC

Experimental and Numerical Study on the Bending Behavior of Satin-Woven SiCf/SiC Composites

Experimental and numerical study of in-plane compressive properties and failure of 3D six-directional braided composites with large braiding angle

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Failure Analysis of Carbon Fiber Reinforced Composite Subjected to Low Velocity Impact and Compression after Impact

Fabrication and Mechanical Behavior of Carbon Fiber Composite Sandwich Cylindrical Shells with Corrugated Cores

Mechanical Properties Investigation of Carbon/carbon Composites Fabricated by a Fast Densification Process

An Experimental Study on the Fracture of a Unidirectional Carbon Fiber-Reinforced Composite under Quasistatic Torsion

Experimental characterization of failure behaviour for three-dimensional woven carbon/carbon composites under pin-loading

Experimental Study on the Mechanical Behavior and Failure Mechanism of 3d MWK Carbon/epoxy Composites under Quasi-Static Loading

Micromechanical modeling of longitudinal compression behavior and failure mechanism of unidirectional carbon fiber reinforced aluminum composites involving initial fiber misalignment

Mechanical Behaviors of the Three-Dimensional Woven Carbon/carbon Composite Materials under Biaxial Compression

Mechanical behaviors of the composites reinforced by non-crimp unidirectional carbon fiber fabrics under biaxial compression loading

Real-Time Observation of Damage Nucleation in Three-Dimensionally Reinforced Carbon/Carbon Composites and Role of Bundle/Matrix Interface

Experiment investigation on biaxial tensile strength of 3D in-plane braided C/C composites

Exploring the influence of specimen types on the intralaminar fracture behavior of fiber-reinforced polymer matrix composites