Abstract:The interface properties between surface grown carbon nanotubes carbon fiber (CNTs‐CF) and epoxy resin were investigated by different modification methods. The X‐ray photoelectron spectrometer probations show that the pristine CNTs‐CF has very low contents of both oxygen element and active carbon element. Taking the naked carbon fiber (CF) without CNTs grown as a reference, the interfacial shear strength (IFSS) of CNTs‐CF/epoxy is only 5.6% higher. After heat treatment, chemical modification and sizing treatments, the surface chemical activity of CNTs‐CF is improved considerably. In contrast with the IFSS of standard CF/epoxy, the interfacial strength of chemical‐treated CNTs‐CF‐E1/epoxy is increased to 122.8 MPa by 29.7%. The increasing content of the epoxy active groups at the modified CNTs‐CF‐E1 surface is conducive to forming covalent bonds between the epoxy resin and the CNTs‐CF‐E1 surface particularly the activated nanotube surface. The enhancement of CNT/epoxy interface is beneficial to the over whole interface property of the composites. Hence, the compressive and torsion strength of sizing CNTs‐CF‐E1 bundle combined with epoxy resin are increased by 32.4% and 14.1%, respectively. The SEM images show the failure morphologies of different modification methods, and the enhancement mechanism of multiscale interface is further clarified. Compared with chemical treatment, heat treatment can remove the inert amorphous carbon on the CNTs‐CF fiber surface and improve the interface adhesion of CNT/epoxy and CF/epoxy, and surface sizing treatment improves the CF/epoxy interface. The enhancement mechanisms of these modified CNTs‐CFs/epoxy should be ascribed to the competition and synergetic effects of the multiscale interfaces, including CNT/CF, CNT/epoxy, and CF/epoxy.

Interface enhancement of carbon nanotube/mesocarbon microbead isotropic composites

Carbon-nanotube-templated Carbon Nanofibers with Improved Mechanical Performance

Interfacial Strengthening and Self-Monitoring in Carbon Fiber-Reinforced Composites via Carbon Nanotube-Based Damage Sensors

Reducing Dispersity of Mechanical Properties of Carbon Fiber/epoxy Composites by Introducing Multi-Walled Carbon Nanotubes

Fabrication and mechanical properties of in situ prepared mesocarbon microbead/carbon nanotube composites

TiC-modified CNTs as reinforcing fillers for isotropic graphite produced from mesocarbon microbeads

Optimization of the mechanical properties of CNTs/Cu composite by regulating the size of interfacial TiC

Influence of Carbon Nanotube Coatings on Carbon Fiber by Ultrasonically Assisted Electrophoretic Deposition on Its Composite Interfacial Property.

On the role of carbon nanotubes addition in carbon fiber-reinforced magnesium matrix composites

Improving thermal shock and ablation resistance of high thermal conductivity carbon/carbon composites by introducing carbon nanotubes

Regulating the mechanical properties and electrical conductivity of CNTs/Cu composites by tailoring nano-sized TiC on the surface of intact CNTs

Prickly structure of multi-walled carbon nanotube reinforced mesocarbon microbead composite with high strength at elevated temperature

Multiscale interfacial enhancement of surface grown carbon nanotubes carbon fiber composites

Interfacial modification of carbon fiber by carbon nanotube gas-phase dispersion

Enhancement of thermal–mechanical performances via a selective CNTs configuration in laminated CNTs/AZ31B composite

Nano-interface effect of graphene on carbon nanotube reinforced carbon/carbon composites

Enhancement of mechanical properties and conductivity in carbon nanotubes (CNTs)/Cu matrix composite by surface and intratube decoration of CNTs

Carbon fiber/epoxy composite property enhancement through incorporation of carbon nanotubes at the fiber-matrix interphase – Part II: Mechanical and electrical properties of carbon nanotube coated carbon fiber composites

Interface design of carbon fiber composites by fabricating interlocked carbon nanotubes-silicon nitride nanowires

Improvement of interfacial interaction and mechanical properties in aluminum matrix composites reinforced with Cu-coated carbon nanotubes

Enhanced load transfer by designing mechanical interfacial bonding in carbon nanotube reinforced aluminum composites