Flow Stress Behavior of Cu-Ag Alloy under Hot Compression Deformation

王梦寒,黄龙,咸国材

DOI: https://doi.org/10.3969/j.issn.0258-7076.2013.05.003

2013-01-01

Abstract:The hot flow stress behavior of Cu-Ag alloy was studied by hot compression tests at the strain rates of 0. 01 ~ 10. 00 s- 1and the temperatures of 700 ~ 850 ℃. The results showed that the high-temperature flow stress of the alloy was sensitive to temperature and strain rate,and softening characteristics were different under the different conditions. Through hyperbolic sine constitutive equation and analysis of linear regression,6 times polynomial equations under different deforming conditions were obtained about structure factor A,the material parameters α,n and the hot deformation activation energy Q. Thus,the flow stress constitutive equation of alloy was established. The processing map of Cu-Ay alloy was set up through the power dissipation map and instability map which were established based on the dynamic material modeling( DMM). Then the processing zone and flow instability region based processing map were determined. The results showed that the optimal deformation parameters included three areas: the low temperature and low strain rate region( deformation temperature of 700 ~ 770 ℃,strain rate of 0. 0100 ~ 0. 0316 s- 1),in which the maximum power dissipation coefficient η was 0. 46; high temperature and medium strain rate region( deformation temperature of 780 ~ 835 ℃,strain rate of 0. 1 ~1. 0 s- 1),in which the maximum power dissipation coefficient η was 0. 33; and high temperature and high strain rate( deformation temperature of 835 ~ 850 ℃,strain rate of 3. 162 ~ 10. 000 s- 1),in which the maximum power dissipation coefficient η was 0. 33.