Abstract:Highly ordered mesoporous polymer-silica and carbon-silica nanocomposites with interpenetrating networks have been successfully synthesized by the evaporation-induced triconstituent co-assembly method, wherein soluble resol polymer is used as an organic precursor, prehydrolyzed TEOS is used as an inorganic precursor, and triblock copolymer F127 is used as a template. It is proposed for the first time that ordered mesoporous nanocomposites have "reinforced concrete"-structured frameworks. By adjusting the initial mass ratios of TEOS to resol, we determined the obtained nanocomposites possess continuous composition with the ratios ranging from zero to infinity for the two constituents that are "homogeneously" dispersed inside the pore walls. The presence of silicates in nanocomposites dramatically inhibits framework shrinkage during the calcination, resulting in highly ordered large-pore mesoporous carbon-silica nanocomposites. Combustion in air or etching in HF solution can remove carbon or silica from the carbon-silica nanocomposites and yield ordered mesoporous pure silica or carbon frameworks. The process generates plenty of small pores in carbon or/and silica pore walls. Ordered mesoporous carbons can then be obtained with large pore sizes of approximately 6.7 nm, pore volumes of approximately 2.0 cm(3)/g, and high surface areas of approximately 2470 m(2)/g. The pore structures and textures can be controlled by varying the sizes and polymerization degrees of two constituent precursors. Accordingly, by simply tuning the aging time of TEOS, ordered mesoporous carbons with evident bimodal pores at 2.6 and 5.8 nm can be synthesized.

Synthesis of Mesoporous Carbon/Silica Using the Oligomer of Urea-formaldehyde Resin As Carbon Source and the Influence of Carbonization Temperature

Facile synthesis of ordered mesoporous carbon with finger citron residue as carbon precursor

Synthesis of mesoporous silica using urea–formaldehyde resin as an active template

Electron Microscopy and Nitrogen Adsorption Studies of Film-Type Carbon Replicas with Large Pore Volume Synthesized by Using Colloidal Silica and Sba-15 As Templates

Synthesis of Mesoporous Silica Materials via Nonsurfactant Urea-Templated Sol-Gel Reactions

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

Ordered Mesoporous Silicas And Carbons With Large Accessible Pores Templated From Amphiphilic Diblock Copolymer Poly(Ethylene Oxide)-B-Polystyrene

Triconstituent Co-Assembly to Ordered Mesostructured Polymer-Silica and Carbon-Silica Nanocomposites and Large-Pore Mesoporous Carbons with High Surface Areas.

Preparation of Mesoporous Carbons from Acrylonitrile-methyl Methacrylate Copolymer/Silica Nanocomposites Synthesized by In-Situ Emulsion Polymerization

High-temperature Synthesis of Ordered Mesoporous Silicas from Solo Hydrocarbonsurfactants and Understanding of Their Synthetic Mechanisms

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

Facile Preparation, Structural Control and Spheroidization of Mesoporous Carbons Using Hydrolyzed Water Glass As a Template

Synthesis of Mesoporous Carbon Using Halloyiste As Template

Synthesis and Characterization of Functionalized Mesoporous Ethanesilica

Synthesis of Ordered Mesoporous Carbons Using Resorcinol-Formaldehyde Sol As the Carbon Source and As-synthesized MCM-48 As the Template

Porous carbon/silica composite monoliths derived from resorcinol–formaldehyde/TEOS

Characterization of the dependence on temperature of the formation of carbon film on the internal surfaces of SBA-15 silica

Direct synthesis of highly ordered amine-functionalized mesoporous ethane-silicas

Preparation and characterization of ordered mesoporous carbons on SBA-15 template

Organosilane-assisted Synthesis of Ordered Mesoporous Poly(furfuryl Alcohol) Composites