Modern experimental verifications of shear mechanism of martensitic transformation and calculation of shear energy——Comment on "non-shear mechanism of martensitic transformation" again

张骥华,戎咏华

DOI: https://doi.org/10.13251/j.issn.0254-6051.2013.05.016

2013-01-01

Abstract:Several modern experiments were selected to prove the correctness of shear mechanism of martensitic transformation. In a lot of non-ferrous alloys the shear energy is large compared with driving force of martensitic transformation, however, the measurements of elastic constants indicate that the elastic constants of parent phase will soften along special direction (which corresponds to shear direction), and this effect will effectively lower the shear energy of martensitic transformation accompanying shear nucleation. The observation of transmission electron microscope (TEM) indicates that the straight trace of a stacking fault will change to terraced when the stacking fault will be sheared by a single variant of martensite, moreover, the shear angle measured is well consistent with the shear angle calculated. High resolution TEM image reveals that there are a transition region near the interface between martensite and austenite, and atoms in the region are at the position shifted by 50% from the original (111) of fcc austenite, which is different from the interface between bainite and austenite produced by diffusing transformation. The calculation method of shear energy for Fe-C alloys proposed by Hsu T Y(Xu Zuyao) was introduced, and the "non-shear mechanism of martensitic transformation" proposed by Liu Zongchang was also commented. It is pointed out that the incorrect calculation of shear energy by liu is attributed to the improper physical concept and lack of deep understand of the previous researches, which results in the error conclusion of "non-shear mechanism of martensitic transformation".