Effect of Zr on Structure and Properties of Ti–Al–N Coatings with Varied Bias

Bing Yang,Li Chen,Yu X. Xu,Ying B. Peng,Ji C. Fen,Yong Du,Ming J. Wu

DOI: https://doi.org/10.1016/j.ijrmhm.2013.01.002

2013-01-01

Abstract:Ti–Al–N coatings exhibit considerable mechanical and thermal properties, which make them promising candidates for advanced machining and other high temperature application. Here, the effect of Zr addition on the structure, mechanical and thermal properties of Ti–Al–N coatings deposited by industrial cathodic arc evaporation system is studied. Furthermore, we researched the machining application of Ti–Al–Zr–N coated inserts with varied bias from −50 to −150V. Addition of Zr leads to a structural transition from cubic to mixed cubic–hexagonal, and an increased hardness from ~31.2 to 33.1GPa. The high hardness value of ~35.8GPa for Ti–Al–Zr–N coating after annealing at 1000°C indicates the improved thermal stability. Oxidation experiments yield fully oxidized Ti–Al–N coating for 16h at 850°C, whereas Ti–Al–Zr–N coating only forms of a layered oxide scale ~1.0μm. Therefore, an increased machining performance in continuous turning is obtained by Ti–Al–Zr–N coated insert. Increasing of deposition bias favors the growth of cubic structure, and thereby results in a structure transition from a mixed cubic–hexagonal structure to finally a single phase cubic structure for bias of −150V. With consideration of its structure, hardness, defect densities, stress and cohesion with substrate, Ti–Al–Zr–N coated inserts with bias of −100V behaved the best performance in both continuous turning and milling.