Effect of cold rolling on microstructure and mechanical properties of pure Zr
Z.N. Yang,Y.Y. Xiao,F.C. Zhang,Z.G. Yan
DOI: https://doi.org/10.1016/j.msea.2012.07.056
2012-10-01
Abstract:Though the resultant microstructure and mechanical properties of pure Zr after severe plastic deformation have been studied, the microstructural evolution and the variation of mechanical properties with progressive deformation of pure Zr have not been investigated in detail. Microstructure observation verified that dislocation slip dominated the plastic behaviour of pure Zr during room temperature deformation. With the increase in the rolling reduction (RZr) from zero to 90%, the various microstructural features, e.g. dislocation tangles, dislocation lamellas, dislocation cells or subgrain structure, and nano-crystal grains (∼72nm), etc., successively occurred. Dynamic recovery played an important role on the plastic behaviour of the pure Zr with high stacking fault energy (SFE), which slowed down the work hardening rate during high strain rate rolling deformation and caused strain softening on the pre-deformed specimens during low strain rate tension deformation. The specimens annealed at 450–600°C not only possessed higher ultimate tensile strength and yield strength, but exhibited higher elongation as compared with the undeformed specimen. The fracture mode of all annealed specimens was entirely dimple fracture.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering