Abstract:Summary form only given. Polycrystalline samples La2/3Caι/3(Mnι_xCox)θ3 with x=0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by standard solid-state reaction. X-ray diffraction results show that they are of single phase for the specimens with x<;0.3. Rietveld refinement of X-ray diffraction data shows Mn-O-Mn angle decreases from 178.8° for x=0.1 to 128.8° for x=0.3. A metal-to-insulator transition was only observed in sample with x=0.1. The different transport properties of these samples were attributed to the different Jahn-Teller distortion. The temperature dependence of reisitivity at low and high temperature can be described by the small polaron model and Kondo-like effect. In the present work, effect of Co doping at B-site of La2/3Caι/3Mnθ3 (LCMO) is discussed. The spin configuration of Co is very complex. The Co ions are in their low-spin (LS) tg6e2g0 (S=0) state at the low temperature (T<;35 K) and high-spin (HS) tg4e2g2 (S=2) state at high temperature (300 K<;T<;600 K). There maybe a intermediate-spin (IS) tg5e2gl (S=l) state or a mixture of HS and LS of Co3+ in the interval 35 K<;T<;100 K. The structure and properties are close dependent on the Co dopant as discussed below. Polycrystalline samples La,/3Ca2/3(Mnι_xCox)θ3 (LCMCO) with x=0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by standard solid-state reaction. The analytical purity materials La203, CaC03, Mn02 and Co203 were well mixed in stoichiometric proportions and pestle for 30 minutes before calcined at 1000 °C for 6 hours. The calcined powder was pressed into slices and then sintered at 1400°C for 32 hours in air. All the specimens were slowly-cooled to room temperature in air for about 15 hours. The structure of the samples was characterized by X-ray diffraction (XRD), which was performed at a Rigaku Dmax-γB diffractometer at room temperature with step scanning model. The struct- ral parameters were obtained from a standard Rietveld program GSAS. The resistivity with/without magnetic field were measured by the standard four-probe method at a Quantum Design PPMS. Measurements of x-ray diffraction at room temperature show that samples within x<;0.3 are of single phase which can be well refined in orthorhombic symmetry with the space group of Prima (Rwp<;15%). The lattice parameters of a, b, and c are almost independent of the Co dopant which indicates the unit cell is unchanged after Co was doped in LCMO. The bond angle of Mn-Ol-Mn decreases largely from 178.8° for x=0.1 to 128.8° for x=0.3. It will induce the large change of electric transport properties as discussed below.

Crossover Effect of Inter-Granular Transport and Quantum Correction in Co-doping La2/3Ca1/3MnO3 Manganites

Magnetic and transport properties of the Co-doped manganite La0.7Sr0.3Mn1-xCoxO3 (0 ≤x ≤ 0.5)

HE ELECTICAL-RANSPORT PROPERTIES OF THE MO-DOPING La0.7Ca0.2Ba0.1Mn1-xMoxO3

Effect of Cu doping at the Mn site on the transport and magnetic behaviors of La2/3Ca1/3MnO3

Effect of Cu doping at the Mn site on the transport aaand magnetic behaviors of La 2/3 Ca 1/3 MnO 3

Cu Doping Effect on Mn Sites of La 2/3 Ca 1/3 MnO 3 System

Magnetic and Transport Properties of Cobalt Doped La0.7Sr0.3MnO3

Effect of Low Fe3o4 Doping in La0.67ca0.33mno3

A comparative study of low-field magnetoresistance for La2/3Ca1/3Mn1-xCuxO3 (x = 0% and 4%) synthesized at different temperatures

Effect of Co doping at the B-site on the structure and tranport properties in La2/3Ca1/3MnO3

Magnetic Field Mediated Low-Temperature Resistivity Upturn In Electron-Doped La1-Xhfxmno3 Manganite Oxides

Magneto-transport and specific heat behavior of Cd-doped LaCaMnO

The Significant and Temperature-Insensitive Magnetoresistance Observed in Co-doped (la0.7sr0.3)mno3 Thin Films

Singular Behavior Observed in the Low Temperature Electronic Transport and Thermodynamic Properties of Mn Doped Na0.68coo2

Electric and Magnetic Behaviour in Double Doped La2/3+4x/3Sr1/3−4x/3Mn1−xMgxO3

Effect of Cobalt on the Magnetoresistance Characteristics of Rare-Earth Doped Manganites

Magnetic Phase Boundary and Transport Properties of La0.67Ca0.33MnO3

Coexistence of Charge Ordering and Ferromagnetism in Nd0.5Ca0.5Mn1−xCoxO3 (x ≤ 0.1)

Low Temperature Transport Behavior and Kondo Scattering in Dilute Mn-doped NaγCo1−xMnxO2

Comparative study of electrical transport of (1-x)La0.67Ca0.67MnO3/xCuO and La0.67Ca0.33 Mn1-xCuxO3

A comparative study of low-field magnetoresistance for La<sub>2/3</sub>Ca<sub>1/3</sub>Mn<sub>1 <i>x</i></sub>Cu<sub><i>x</i></sub>O<sub>3</sub>(<i>x</i> 0 and 4 ) synthesized at different temperatures