Abstract:The microstructure and mechanical characteristics of the AZ61 magnesium alloy with varying RE (RE) content during the extrusion-forging process were thoroughly examined using metallography, SEM, EDS, and XRD. Findings indicate that as the RE content increases, the β-Mg 17 Al 12 phase is significantly diminished, primarily resulting in a microstructure composed of Al 4 Ce and Al 8 Mn 4 Ce phases or Al 3 Nd and Al 4 Ce phases, along with a minor presence of Al 4 La phase, which appears in black granular or agglomerated forms along the extrusion axis. Following die forging, the RE phases in the AZ61+xRE Mg alloy's microstructure experienced secondary fragmentation due to triaxial compressive stress, leading to a drum-shaped or S-shaped distribution of the fractured RE material, without any spheroidization or new phase formation occurring during deformation, while the β-Mg 17 Al 12 phase was entirely dissolved in the matrix. Post die forging, the mechanical properties of the AZ61+xRE magnesium alloy showed significant enhancement, with the AEZ641 alloy exhibiting the highest increases in tensile strength and yield strength, at 8.5 and 26.2%, respectively. Nonetheless, the elongation of all four alloys decreased markedly, by 42 to 52%, and hardness increased by 3.5 to 7.1%. As RE content rose, the yield strength, tensile strength, elongation, and hardness of the as-forged AEZ611 alloy reached values of 220 MPa, 302.3 MPa, 11.25%, and 65.8 HRE, respectively, showcasing the best overall mechanical properties at room temperature. During the transition from extrusion to die forging, the macrofracture exhibited distinct necking, while the microfracture revealed numerous pits, with a significant presence of second phase or RE particles located at the pits' bottoms. The fracture mechanism was identified as a mixed fracture with characteristics of toughness.

Effect of rare earth elements on deformation behavior of an extruded Mg-10Gd-3Y-0.5Zr alloy during compression

Cyclic Deformation Behavior of a Rare-Earth Containing Extruded Magnesium Alloy: Effect of Heat Treatment

Synergistic Effects of Cerium-Based Rare Earth Addition and Hot Deformation on the Microstructure and Mechanical Properties of Mg-0.5Zn-0.5Zr Magnesium Alloy

Cyclic Deformation Of Rare-Earth Containing Magnesium Alloys

Effect of Double Plastic Deformation on Microstructure and Mechanical Properties of High-Content Rare-Earth AZ61 Mg Alloy

Improved mechanical performance of double-pass extruded Mg-Gd-Er-Zr alloys with various rare earth contents

Effects of the Extrusion Parameters on Microstructure, Texture and Room Temperature Mechanical Properties of Extruded Mg–2.49Nd–1.82Gd–0.2Zn–0.2Zr Alloy

Microstructure, Texture, and Enhanced Mechanical Properties of an Extruded Mg–rare Earth Alloy after Hot Compression

Low cycle fatigue of a rare-earth containing extruded magnesium alloy

Deformation Behavior, Microstructure Evolution and Hot Workability of Mg-3.7Gd-2.9Y-0.7Zn-0.7Zr Alloy

High Temperature Compressive Deformation Behavior of an Extruded Mg–8Gd–3Y–0.5Zr (wt.%) Alloy

Effects of the Extrusion Temperature on Microstructure, Texture Evolution and Mechanical Properties of Extruded Mg-2.49Nd-1.82Gd-0.19Zn-0.4Zr Alloy

Effects of RE on Microstructures and Mechanical Properties of Hot-Extruded AZ31 Magnesium Alloy

Tension-compression Asymmetry of Extruded Mg-Gd-Y-Zr Alloy with a Bimodal Microstructure Studied by In-Situ Synchrotron Diffraction

Correlation Between Dynamic Recrystallization and Formation of Rare Earth Texture in a Mg-Zn-Gd Magnesium Alloy During Extrusion

Deformation Mechanisms of Magnesium Alloys with Rare-Earth and Zinc Additions under Plane Strain Compression

Study on extrusion process of Mg-10Gd-8Y-1.5Nd-0.5Zr alloy intensified with rare earth elements

Effects of temperature and strain rate on deformation behaviors of an extruded Mg-5Zn-2.5Y-1Ce-0.5Mn alloy

Deformation Behavior and Dynamic Recrystallization of Mg-Y-Nd-Gd-Zr Alloy

Bimodal Grain Structure, Phase Transformation, and Mechanical Properties of a Mg-Gd-Y-Zn-Zr Alloy During Hot Extrusion

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-7.5Gd-2.5Y-3.5Zn-0.9Ca-0.4Zr (wt%) Alloy