Microwave Dielectric Properties of Li2tio3 Ceramics Doped with Lif for Ltcc Applications

Yi-Zhou Hao,Hui Yang,Guo-Hua Chen,Qi-Long Zhang

DOI: https://doi.org/10.1016/j.jallcom.2012.10.110

IF: 6.2

2013-01-01

Journal of Alloys and Compounds

Abstract:Sintering characteristics and microwave dielectric properties of LiF (<= 4.0 wt%) doped Li2TiO3 ceramics were studied in this paper. The phase presence, surface morphology and according energy dispersive spectrometer (EDS) analysis were determined by X-ray diffractometer (XRD) and scanning electron microscope (SEM) techniques, respectively. The addition of LiF as sintering aid can effectively reduce the sintering temperature of Li2TiO3 ceramics, and well-densified microwave ceramics with uniform grains could be obtained under 950 degrees C. Continuous solid solution formed for all doped samples in which LiF was uniformly distributed in the matrix. In addition, it is found that 1.0-3.0 wt% amount of LiF can significantly improve microwave dielectric properties of Li2TiO3 ceramics. The temperature coefficient of resonant frequency (tau(f)) decreased with increasing the amount of LiF addition. Typically, optimum dielectric microwave of epsilon(r) = 24.01, Q x f = 75,500 GHz, and tau(f) = 36.2 ppm/degrees C was achieved for 2.5 wt% LiF doped samples sintered at 950 degrees C for 3 h. The chemical compatibilities of 2.5 wt% LiF doped ceramics with silver were also investigated. The low-temperature sintering ceramics are compatible with Ag electrodes, and therefore, suitable for low-temperature co-fired ceramics (LTCC) application. (C) 2012 Elsevier B. V. All rights reserved.