Process optimization for degradation of crystal violet by ferric-carbon micro-electrolysis using Box-Behnken response surface methodology

宿程远,李伟光,王勇,李云蓓

2013-01-01

Abstract:Base on the single factor test, the Box-Behnken response surface methodology was utilized for modeling and optimization conditions on degradation of crystal violet by ferric-carbon micro-electrolysis. In this case, decolorization rate was selected as one response value, while the ratio of ferric to carbon, aeration rate and reaction time were considered as influential factors. At the same time, the mathematical model was established between the decolorization rate and the three influential factors. The results showed that when the initial concentration was 100 mg/L and volume was 300 mL, the decolorization rate could reach 89.6% with the ratio of ferric to carbon of 2:1, the aeration rate of 20 L/h, the dosage of ferric of 20 g, the pH of 3 and the reaction time of 80 min. The ratio of ferric to carbon, aeration rate, reaction time, the interaction of ratio of ferric to carbon and reaction time were all significant factors. Especially, the aeration rate on the decolorization rate was particularly significant. The determinate coefficient of model was 0.9067 and the probability p value was 0.039. It showed that the model fitting degree was good, and the model was significant. The optimum conditions were as follows: the ratio of ferric to carbon of 2.4:1, aeration rate of 40 L/h and reaction time of 84 min. Under such conditions, the decolorization rate was 93.25% and the error of the model-predicted and experimental values of decolorization rate was 2.26%.