Microstructure and deformation mechanism of high strain line pipe

Haitao Wang,Lingkang Ji,Chenshuai Huang,Hongyuan Chen,Chi Qiang,Yang Li

DOI: https://doi.org/10.1061/9780784413142.110

2013-01-01

Abstract:Strain-hardening mechanism of high strain line pipe was investigated and discussed in terms of microstructure and grain orientation. It is concluded that X70 high strain line pipe does not fit to the Hollimon formula in the entire deforming process, but the normal X70 line pipe does. At the beginning of plastic deformation, the strain-hardening capacity of X70 high strain line pipe is excellent. It decreases rapidly as the stain increases, then becomes stable after 2.0% total strain. The high strain line pipe is composed of soft phase (polygonal ferrite) and hard phase (bainite). When plastic deformation initiates, the strain-hardening capacity of high strain line pipe is better because of the ferrite deformation firstly ahead of the bainite, due to strain-hardening capacity of the ferrite is much better than that of the bainite. With ferrite deformation decreasing and bainite deformation increasing, the strain-hardening capacity declines until the micro-deformation is homogeneous. Besides, it is obvious that the large angle grain boundaries of more than 15° are in the majority of the microstructure of high strain line pipe without deformation, so the strain-hardening capacity is highest at the beginning of plastic deformation. As strain increases, the large angle grain boundaries decrease, and the small angle grain boundaries increase, then the strain-hardening capacity falls down. When the proportion of large angle grain boundaries and small angle grain boundaries becomes stable, the strain-hardening capacity is also stable. © ASCE 2013.