Abstract:In order to study the space charge behavior of imported DC cable's XLPE material at high temperatures, we prepared undegassed and degassed XLPE samples for the tests, including DC conduction, dielectric and space charge during steady and transient processes at high temperatures. The results show that both the conduction current and dielectric loss of undegassed XLPE are larger than those of degassed XLPE. Negative charge accumulation is observed in the bulk of degassed and undegassed XLPE under-30 MV/m, and the distortion ratio of internal electric fields is below 25％ at 30 ℃ and 70 ℃. A positive space charge packet appears and subsequently moves quickly within the first 2 s polarization under-100 MV/m at 70 ℃. However, the injection and migration of a negative space charge packet can only be observed when the applied field raises to-150 MV/m. Here, both polarities of space charge packets follow negative differential mobility. The analyses reveal that degassing treatment can effectively reduce the amount of crosslinking byproducts in XLPE, resulting in the decrease of ionization and conductivity in low frequency regions. A small amount of negative charge accumulating in the bulk is produced mainly by the ionization of crosslinking byproducts and impurities, but the positive charge is injected from the anode with the increase of electric field, and the rate of impurity ionization is higher than the positive charge injection rate. During the initial stage of polarization processes under-150 MV/m at 70 ℃, the fast transit of positive charge leads to the severe distortion of the local field near the cathode (up to 61.5％), resulting in a large amount of negative charge injection and the formation of a negative space charge packet in the bulk.

Thickness Dependence of Space Charge in XLPE and Its Nanocomposites under Temperature Gradient

Study of the Space Charge Behavior in Polyethylene Nano-Composites under Temperature Gradient

Dependence of Charge Accumulation on Sample Thickness in Nano-SiO2 Doped IDPE

Mechanism Of Space Charge Accumulation In Crosslinked Polyethylene Under Temperature Gradient

Electrical Insulation Performance of Cross‐linked Polyethylene/mgo Nanocomposite Material for ±320 Kv High‐voltage Direct‐current Cables

Space Charge Characteristics in XLPE/BN Nanocomposites at Different Temperatures

Effect of Thermal Ageing on Space Charge Behavior of HVDC XLPE Materials

Space charge behavior in polypropylene/polyolefin elastomer/MgO nanocomposites under temperature gradient

Space Charge Behavior of XLPE After Long-term Aging Under Temperature Gradient and Under DC Stress

Temperature and Electric Field Dependence of Charge Conduction and Accumulation in XLPE Based on Polarization and Depolarization Current

Study on Space Charge Behavior of XLPE after Long-Term Aging under Temperature Gradient and DC Stress

Temperature Effect of Space Charge Distribution in Cross-Linked Polyethylene

Effect of Temperature Gradient on Space Charge Behavior in Epoxy Resin and Its Nanocomposites

Charge Transport Behavior in XLPE-insulated Cables under DC and Thermal Gradient Coupling Field Considering the Effects of Non-Uniform Conductivity

Space Charge Characteristics in 160 Kv DC XLPE Cable under Temperature Gradient

Analysis of Influence Factors on Space Charge Accumulation Characteristics of 320 kV XLPE Cable

Space Charge Behavior of DC Cable's XLPE Material at High Temperatures

Effect of thermal ageing on charge dynamics and material properties of 320 kV HVDC XLPE

Space Charge Measurement in LPDE Films under Temperature Gradient and DC Stress

Effect of Temperature on Trap Depth in Polyethylene Nannocomposite

Space Charge Accumulation and Stress Distortion in Polyethylene Under High DC Voltage and Temperature Gradient