Abstract:In order to study the space charge behavior of imported DC cable's XLPE material at high temperatures, we prepared undegassed and degassed XLPE samples for the tests, including DC conduction, dielectric and space charge during steady and transient processes at high temperatures. The results show that both the conduction current and dielectric loss of undegassed XLPE are larger than those of degassed XLPE. Negative charge accumulation is observed in the bulk of degassed and undegassed XLPE under-30 MV/m, and the distortion ratio of internal electric fields is below 25％ at 30 ℃ and 70 ℃. A positive space charge packet appears and subsequently moves quickly within the first 2 s polarization under-100 MV/m at 70 ℃. However, the injection and migration of a negative space charge packet can only be observed when the applied field raises to-150 MV/m. Here, both polarities of space charge packets follow negative differential mobility. The analyses reveal that degassing treatment can effectively reduce the amount of crosslinking byproducts in XLPE, resulting in the decrease of ionization and conductivity in low frequency regions. A small amount of negative charge accumulating in the bulk is produced mainly by the ionization of crosslinking byproducts and impurities, but the positive charge is injected from the anode with the increase of electric field, and the rate of impurity ionization is higher than the positive charge injection rate. During the initial stage of polarization processes under-150 MV/m at 70 ℃, the fast transit of positive charge leads to the severe distortion of the local field near the cathode (up to 61.5％), resulting in a large amount of negative charge injection and the formation of a negative space charge packet in the bulk.

Study of the Space Charge Behavior in Polyethylene Nano-Composites under Temperature Gradient

Space charge behavior in polypropylene/polyolefin elastomer/MgO nanocomposites under temperature gradient

Electrical Insulation Performance of Cross‐linked Polyethylene/mgo Nanocomposite Material for ±320 Kv High‐voltage Direct‐current Cables

Electrical Treeing in Polyethylene-Alumina-filled Nanocomposites for HVDC Applications

Insulating Properties of Low Density Polyethylene/Alumina Nanocomposites

Space charge performance of epoxy composites with improved thermal property at high temperature under high electric field

Space Charge Dynamics in Epoxy Based Composites under DC and Square Pulse Wave of Different Polarities and Frequencies

Space Charge Suppression of Polyethylene Induced by Blending with Ethylene-Butyl Acrylate Copolymer

Effect of Nano-Al2O3 on Insulating Properties of Low-density Polyethylene Nanocomposites for HVDC Cables

Space Charge Behavior in LDPE/EBA Insulation Materials for HVDC Cables

Preparation, Microstructure and Properties of Polyethylene/alumina Nanocomposites for HVDC Insulation

Effect of Thermal Ageing on Space Charge Behavior of HVDC XLPE Materials

Space Charge Accumulation between Different Insulating Materials Simulated Cable Joint for HVDC

Fast space charge packet characteristics within low-density polyethylene affected by epitaxial crystallization

Influence of hierarchy structure on electrical properties of gradient-distribution aluminum oxide/polyethylene nanocomposites

Space Charge Accumulation at Material Interfaces in HVDC Cable Insulation Part I—Experimental Study and Charge Injection Hypothesis

Analysis of Influence Factors on Space Charge Accumulation Characteristics of 320 kV XLPE Cable

Sandwiched Structure Effect on Space Charge Characteristics of Alumina/polyethylene Nanocomposites

Study on space charge accumulation characteristics of 320 kV cross-linked polyethylene cable joints

Influence of Thermal Aging on Space Charge Characteristics and Electrical Conduction Behavior of Cross-Linked Polyethylene Cable Insulation

Space Charge Behavior of DC Cable's XLPE Material at High Temperatures