Abstract:To increase the strength and wear resistance of material surface,adding mixed-powder with different mass fraction into Fe901 self-fluxing alloy powder,the composite coatings reinforced by TiC-TiB2 were successfully prepared on 45 steel surfaces by laser cladding.The mixed-powder was the mixture of TiO2,B4 C,C and Al.The phases,microstructure and mechanical properties were analyzed by X-ray diffraction(XRD),scan electron microscopy(SEM),microhardness tester and wear tester.The thermodynamics of each reaction in the system was calculated.The results show that,the interfaces of composite coatings and their substrate material are metallurgically bonded,and the coatings are uniform and dense without cracks and pores.In-situ synthesizing,the phases of TiC and TiB2 are thermodynamically possible.The composite coatings are composed ofα-Fe,TiC,TiB2 and(Fe,Cr)7 C3.The fine block-shaped TiC particles and strip-shaped TiB2 uniformly disperse in the matrix of coatings.They can fine the microstructure further and play the role of precipitation-strength.The size of microstructure and the amount of dendrite decrease markedly after adding the mixed-powder.The more the mixed-powder is,the finer the microstructure becomes.The average microhardness values of the coatings reinforced by TiC-TiB2 are between 720HV0.2 and 760HV0.2,which are 30% higher than that of the coating without TiC-TiB2,and their abrasion resistances increase obviously.The lowest mass loss can be obtained when the mass fraction of mixed-powder is 50%.

In Situ Synthesis of TiC-TiB2 Reinforced Fe-Based Composite Coating by Laser Cladding

In-situ Synthesized TiC-TiB2 Composite Coatings Prepared by Laser Cladding

Microstructure of Fe-Ti-B composite coating prepared by laser cladding

Microstructure and wear properties of TiC/FeCrBSi surface composite coating prepared by laser cladding

Microstructure and Property of Laser Cladding TiC/Fe-based Composite Coating in Al-TiO2-C System

In-Situ Synthetic Tib2 Particulate Reinforced Metal Matrix Composite Coating on Aa2024 Aluminum Alloy by Laser Cladding Technology

TiC reinforced composite coating produced by powder feeding laser cladding

Design, fabrication, microstructure and properties of in-situ synthesized TiC reinforced stainless steel matrix composite coating by laser cladding

TiC particulate composite coating produced in situ by laser cladding

Study on Laser In-Situ Synthesized TiC-TiB2/Fe Composite Coating and Its Oxidation Resistance

In-situ Synthesized TiC/TiB Ceramic Particle Composite Coating by Laser Cladding on TC4 Titanium Alloy

Microstructure and element distribution of laser cladding TiC -reinforced CrTi4-based composite coating with CeO2/Ce2O3

Substructure of Martensite in Particle Reinforced Fe-based Composite Coating by Laser Cladding

Fabrication of nickel composite coatings reinforced with TiC particles by laser cladding

Microstructure Characteristics and Properties of In-Situ Formed Tic/Ni Based Alloy Composite Coating by Laser Cladding

Microstructure and Wear Behavior of In-Situ Synthesized TiC-reinforced CoCrFeNi High Entropy Alloy Prepared by Laser Cladding

Laser Producing Fe-Based Composite Coatings Reinforced by in Situ Synthesized Multiple Carbide Particles

Research on microstructure of in situ synthesized TiB2/Ni metal–ceramics composite coating

An investigation on wear and cavitation erosion-corrosion characteristics of the TiC modified Fe-based composite coating via laser cladding

In Situ Formation of TiC Reinforced Intermetallic-Matrix Composite Layers Produced by Laser Cladding

In Situ Formation of Tic Particulate Composite Coating with A Gradient Distribution by Laser Cladding