Abstract:s The paper uses a laser cladding process to prepare a composite coating of Ni60A and x% TiC (x = 0, 2, 4, 8) by mass percentage on the surface of H13 steel. The effects of different TiC additions on the microstructure and properties of the laser cladding coatings were analyzed by X-ray diffractometer (XRD), non-destructive testing, Penetrant testing (PT), optical microscope (OM), scanning electron microscope (SEM), energy dispersive spectrometer (EDS), micro-hardness tester, friction and wear tester, and electrochemical workstation. The results show that the coating microstructure without TiC addition was dominated by dendrites. The microstructure of the coatings appeared as short rods and equiaxed crystals after the addition of TiC. After analysis, hard reinforcing phases such as Cr 23 C 6 , Cr 7 C 3 , and TiCx were found to have a pinning effect at the grain boundaries, thus hindering the grain boundary slip. These can significantly increase the hardness of the coating. Most of the Ni60A coating with the addition of 2 wt% TiC (C2)coating curve is at the bottom end of the graph line. It has an average friction factor of 1.43 and a low wear weight loss. C2 coatings have less wear than C0 coatings.C2 coatings have 8.5% of the wear of C0 coatings.C2 has the best wear resistance. The hardness of the C2 coating is 662HV0.5, which is higher than other coatings with different TiC additions. The C2 coating had the lowest self-corrosion current of 7.076 ×10–7 A·cm-2. C2 coatings significantly appear grain refinement, lattice distortion, coating hardness, and wear resistance are high, with better corrosion resistance. The strengthening mechanism is mainly solid solution strengthening and fine grain strengthening together.

TiC reinforced composite coating produced by powder feeding laser cladding

Fabrication of nickel composite coatings reinforced with TiC particles by laser cladding

TiC particulate composite coating produced in situ by laser cladding

Microstructure Characteristics and Properties of In-Situ Formed Tic/Ni Based Alloy Composite Coating by Laser Cladding

Research on In-Situ Formation of Tic Particles Reinforced Nickel Base Alloy Coating Produced by Laser Cladding

In Situ Formation of Tic Particulate Composite Coating with A Gradient Distribution by Laser Cladding

In-situ Synthesis of WC/TaC Reinforced Nickel-Based Composite Alloy Coating by Laser Cladding

Research on Microstructure Properties of the TiC/Ni-Fe-Al Coating Prepared by Laser Cladding Technology

Fabrication of Tic Reinforced Ni Based Coating by Laser Cladding

Microstructure Evolution of TiC Particles In Situ, Synthesized by Laser Cladding

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding

Laser cladding Ni-base composite coatings reinforced by in-situ synthesized multiple carbide particles

Synthesis of Y2O3 particle enhanced Ni/TiC composite on TC4 Ti alloy by laser cladding

In-situ Synthesized TiC/TiB Ceramic Particle Composite Coating by Laser Cladding on TC4 Titanium Alloy

Effect of TiC addition on the microstructure and properties of laser cladding Ni60A coatings on H13 steel surface

Effects of Process Parameters on Geometrical Characteristics and Microstructure of TiC Particle-Reinforced Co50 Alloy by Laser Cladding

Microstructure and Performance of Laser Cladding of Ni/TiB2 Composite Coatings

Laser Cladding Ni-Base Composite Coating on Titanium Alloy with Pre-Placed B4C+NiCoCrAlY

Microstructures and Properties of Laser-Clad in Situ Particle Reinforced Ni-Base Composite Coating on 55mn Steel

In situ formation by laser cladding of a TiC composite coating with a gradient distribution

Microstructure and properties of Inconel 718 matrix composite coatings reinforced with submicron TiC particles prepared by laser cladding