Structure and water-lubricated tribological properties of Cr/a-C coatings with different Cr contents

Qianzhi Wang,Fei Zhou,XiangDong Ding,Zhifeng Zhou,Chundong Wang,Wenjun Zhang,Lawrence Kwok Yan Li,Shuittong Lee
DOI: https://doi.org/10.1016/j.triboint.2013.07.002
IF: 5.62
2013-01-01
Tribology International
Abstract:The Cr containing amorphous carbon coatings (Cr/a-C) with varying Cr content were deposited using unbalanced magnetron sputtering. The results revealed that the chromium carbide nano-clusters were formed when the Cr content exceeded 4.9at%. The critical load increased while the hardness decreased after the Cr element incorporation. Although the low Cr containing Cr/a-C coatings (≤4.9at%) exhibited similar friction coefficient with a-C coatings, but the initial friction coefficient, running-in distance and wear rate of SUS440C balls all decreased. However, the Cr/a-C coatings with high Cr content (11.98–14.09at%) would worsen the tribological properties because chromium carbides acted as abrasive wear particles during tribotests.
What problem does this paper attempt to address?