Abstract:3D Ti6Al4V-beta-tricalcium phosphate (TCP) hybrid scaffolds with interconnected porous network and controllable porosity and pore size were successfully produced by three-dimensional fiber deposition (3DF). The macrostructure of scaffolds was determined by the 3D design, whereas the micro- and submicron structure were derived from the Ti6Al4V powder sintering and the crystalline TCP powder, respectively. Ti6Al4V-TCP slurry was developed for 3DF by optimizing the TCP powder size, Ti6Al4V-to-TCP powder ratio and Ti6Al4V-TCP powder content. Moreover, the air pressure and fiber deposition rate were optimized. A maximum achievable ceramic content in the Ti6Al4V-TCP slurry that enables 3DF manufacturing was 10 wt%. The chemical analysis showed that limited contamination occurred during sintering. The compressive strength and Young's modulus of the scaffolds exhibited values between those of cancellous and cortical bone. The 3D Ti6Al4V-TCP scaffolds with 10 wt% TCP allowed deposition of a calcium phosphate layer on the surface in a simulated body fluid. Cumulative release of calcium and phosphate ions from the scaffolds was observed in a simulated physiological solution, in contrast to a cell culture medium. A pilot in vivo study, in which the scaffolds were implanted intramuscularly in dogs showed ectopic bone formation in the Ti6Al4V-TCP scaffolds with 10 wt% TCP, showing their osteoinductive potential. The porous 3D Ti6Al4V-TCP scaffolds developed here combine the mechanical properties of the metal with the bioactivity of the ceramic and are therefore likely to yield more effective strategies to control the implant-bone interface and thereby improve long-term clinical results in orthopaedics and craniomaxillofacial surgery. STATEMENT OF SIGNIFICANCE: In this work, 3D porous hybrid scaffolds made of a titanium alloy and a beta-tricalcium phosphate ceramic (Ti6Al4V-TCP) were developed using the direct additive manufacturing technique 3D fiber deposition. Upon optimization of the powders and slurry, scaffolds with up to 10 wt.% TCP with good mechanical properties and controllable porous structure at different length scales were successfully manufactured. A preliminary in vivo study in an intramuscular model demonstrated that the addition of TCP to the metal alloy improved its bioactivity. The combination of the two materials and the use of a direct additive manufacturing technique resulted in scaffolds that may lead to more effective strategies to control the implant-bone interface and thereby improve long-term clinical results in orthopaedics and craniomaxillofacial surgery.

Fabrication of HA/β‐TCP Scaffolds Based on Micro‐syringe Extrusion System

Effect of Foreign Ion Substitution and Micropore Tuning in Robocasting Single-Phase Bioceramic Scaffolds on the Physicochemical Property and Vascularization

3D Printing Magnesium-Doped Wollastonite/β-Tcp Bioceramics Scaffolds with High Strength and Adjustable Degradation

Fabrication of Bioceramic Scaffolds with Pre-Designed Internal Architecture by Gel Casting and Indirect Stereolithography Techniques

Fabrication of Β‐tricalcium Phosphate Composite Ceramic Scaffolds Based on Spheres Prepared by Extrusion‐spheronization

Fabrication of Porous Beta-Tricalcium Phosphate with Microchannel and Customized Geometry Based on Gel-Casting and Rapid Prototyping.

Fabrication of porous beta-TCP scaffolds by combination of rapid prototyping and freeze drying technology

Porous Morphology, Porosity, Mechanical Properties Of Poly(Alpha-Hydroxy Acid)-Tricalcium Phosphate Composite Scaffolds Fabricated By Low-Temperature Deposition

Fabrication of β-tricalcium phosphate composite ceramic sphere-based scaffolds with hierarchical pore structure for bone regeneration

Design and Fabrication of Cap Scaffolds by Indirect Solid Free Form Fabrication

Preparation and characterization of porous bioceramic scaffold based on additive manufacturing and gel-casting technology

Polymer-Ceramic Composite Scaffolds: The Effect of Hydroxyapatite and β-tri-Calcium Phosphate

3D porous Ti6Al4V-beta-tricalcium phosphate scaffolds directly fabricated by additive manufacturing

Fabrication of Mesoporous Calcium Silicate/calcium Phosphate Cement Scaffolds with High Mechanical Strength by Freeform Fabrication System with Micro-Droplet Jetting

Techniques for fabrication and construction of three-dimensional bioceramic scaffolds: Effect on pores size, porosity and compressive strength

Fabrication of β-TCP/ Akermanite composite scaffold via DLP and in-situ modification of micro-nano surface morphology for bone repair

Ti/β-TCP Composite Porous Scaffolds Fabricated by Direct Ink Writing

Improvement of Mechanical Properties of Macroporous Β-Tricalcium Phosphate Bioceramic Scaffolds with Uniform and Interconnected Pore Structures

Development of Strong and Tough beta-TCP/PCL Composite Scaffolds with Interconnected Porosity by Digital Light Processing and Partial Infiltration

Fabrication of cancellous-bone-mimicking β-tricalcium phosphate bioceramic scaffolds with tunable architecture and mechanical strength by stereolithography 3D printing

369Fabrication of 3D gel-printed β-tricalcium phosphate/titanium dioxide porous scaffolds for cancellous bone tissue engineering