Abstract:In this study, a hot isostatic pressing (HIP) manufactured SiC particles (SiC p ) reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite was fabricated through ball-milling, HIP, homogenization, hot extrusion, solution treatment, and aging treatment. The results showed the presence of an interfacial reaction layer, MgAl 2 O 4 , around the SiC p , which enhanced the bonding between the particles and the matrix. The aging treatment resulted in the formation of different aging precipitates, which were featured by GP zone for T4, GP zone + η' (metastable MgZn 2 ) + η (stable MgZn 2 ) for T6 and GP zone + η' (metastable MgZn 2 ) for T6I4. The composite samples of T4, T6, and T6I4 exhibited different mechanical properties. Specifically, the elastic modulus was measured as 102.9, 103.4, and 102.3 GPa, the yield strength was 685.3, 598.1, and 619.7 MPa, the ultimate tensile strength was 713.6, 618.9, and 633.3 MPa, and the elongation was 2.2%, 1.8%, and 2.8%, respectively. Furthermore, the corrosion behavior of the composite was evaluated through electrochemical, intergranular corrosion, and exfoliation corrosion. The corrosion current density was found to be 3.17 × 10 −7 , 4.97 × 10 −7 , and 3.67 × 10 −7 A cm −2 , the corrosion potential was measured as −0.70, −0.81, and −0.56 V, and the maximum intergranular corrosion depth was 139.9, 167.8, and 106.2 μm for T4, T6, and T6I4, respectively. The severity of exfoliation corrosion varied, with T4 showing severe pitting, T6 exhibiting moderate pitting, and T6I4 displaying slight pitting. The strengthening mechanism and load transfer strengthening of the composites were discussed in detail based on theoretical calculations, and the anti-corrosion mechanisms were also analyzed.

Microstructure, Mechanical Property and Corrosion Behavior of Interpenetrating (HA + Β-Tcp)/mgca Composite Fabricated by Suction Casting

Microstructure And Characteristics Of Interpenetrating Beta-Tcp/Mg-Zn-Mn Composite Fabricated By Suction Casting

Microstructure, mechanical property and corrosion behaviors of interpenetrating C/Mg-Zn-Mn composite fabricated by suction casting.

Microstructure and characteristics of interpenetrating β-TCP/Mg–Zn–Mn composite fabricated by suction casting

Microstructure and Characteristics of the Metal-Ceramic Composite (Mgca-Ha/tcp) Fabricated by Liquid Metal Infiltration.

Microstructures and Mechanical Properties of Engineered Short Fibre Reinforced Aluminium Matrix Composites

Microstructure, mechanical property, bio-corrosion and cytotoxicity evaluations of Mg/HA composites

Microstructure Evolution and Properties of β-TCP/Mg-Zn-Ca Biocomposite Processed by Hot Extrusion Combined with Multi-Pass ECAP

Microstructure, Mechanical Properties and Wear Resistance of As-Cast Mg-3Al-1Ca-0.4Mn/Tip Magnesium Matrix Composites

Microstructure and properties of a HIP manufactured SiC p reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite

Microstructure, anticorrosion, biocompatibility and antibacterial activities of extruded Mg−Zn−Mn strengthened with Ca

Improvement of the mechanical properties and corrosion resistance of biodegradable β-Ca3(PO4)2/Mg-Zn composites prepared by powder metallurgy: the adding β-Ca3(PO4)2, hot extrusion and aging treatment

Mechanical and Corrosion Tests for Magnesium–Zinc/Ti-6Al-4V Composites by Gravity Casting

Research on corrosion behavior and biocompatibility of a porous Mg-3%Zn/5%β-Ca3(PO4)2 composite scaffold for bone tissue engineering

Microstructure, Mechanical Properties, and Corrosion Resistance of Porous Bio Mg Alloy Scaffolds Prepared via a Novel Method

In vitro degradation and cytotoxicity of Mg/Ca composites produced by powder metallurgy

Microstructure and Corrosion Behavior of Thermal-Sprayed Hydroxyapatite/Magnesium Composite Coating on the Surface of AZ91D Magnesium Alloy

Microstructure, Mechanical Properties, In Vitro Biodegradability, and Biocompatibility of Mg-Zn/HA Composites for Biomedical Implant Applications

Study of the Preparation and Properties of Biomedical Ti–Mg Composites

Mechanical, corrosion and biological behavior of centrifugal casting processed Mg-2Zn-1Mn alloy reinforced with β Tricalciumphosphate (βTCP) for orthopaedic applications

A primary study of the corrosion behavior and superior structure stability of Mg–Ti composites fabricated by high-pressure solid-state sintering