Abstract:Ti–Al3Ti laminated composites have been fabricated through reactive sintering in vacuum using Ti and Al foils with different initial thickness. The aluminum layer was completely consumed resulting in microstructures of well-bonded metal–intermetallic layered composites with Ti residual metal layers alternating with the aluminide intermetallic layers. The MIL composites exhibit a very high degree of microstructural design and control. Microstructure characterization by scanning electron microscopy (SEM), X-ray diffractometry (XRD) and energy dispersive spectroscopy (EDX) has shown that Al3Ti is the only titanium aluminide phase due to the thermodynamics and phase selection of the reaction between Ti and Al through mass diffusion in the presence of liquid Al. The mechanical properties and fracture behavior of the fabricated laminated composites were examined through three-point bending test. The results indicated that the composites exhibited anisotropic features. When the load perpendicular to the laminates was applied, they displayed a step-like or saw-tooth load–displacement response and superior flexural strength as well as fracture toughness, which is also dependent on the number and thickness of individual layers. A non-catastropic fracture was observed in the laminated composites due to the deflection of cracks along the Ti/Al3Ti interface. The Ti layer failed by cleavage mode, showing extensive plastic deformation during the bending process.

Microstructure and Reaction Mechanism of Multi-Laminated Ti-(Sicp/Al) Composites Subjected to Annealing at 1300 Degrees C

Microstructure Evolution of SiCp/Al-Ti Foils During Hot Rolling and Reaction Annealing

Growth Kinetics of TiAl3 Layer in Multi-Laminated Ti–(TiB2/Al) Composite Sheets During Annealing Treatment

Microstructure Evolution of in Situ (ti3alc + Ti5si3)/Ti3al Composite Sheet with A Novel Quasi-Continuous Chain Reinforcement Distribution Architecture Prepared by Using Roll Bonding and Reaction Annealing

Microstructure Evolution of Ti-Al-C System Composite

The Fabrication of Titanium Aluminide Matrix Composite Sheet by Rolling and Reaction Annealing

Influence of Annealing Heat Treatment on the Microstructure and Mechanical Properties of Multilayer 316L-TiC Composite Fabricated by Selective Laser Melting

Formation mechanism and growth kinetics of TiAl3 phase in cold-rolled Ti/Al laminated composites during annealing

Fabrication, Microstructure Characterization and Fracture Behavior of a Unique Micro-Laminated TiB-TiAl Composites

Microstructure and Mechanical Properties of TiBw/Ti-Ti3Al Metal-Intermetallic Laminate (MIL) Composites

Mechanical Properties of (ti2alc+ti3alc)–tial Ceramic–intermetallic Laminate (CIL) Composites

Formation of Intermetallic Compound Layer in Multi-Laminated Ni-(Tib2/Al) Composite Sheets During Annealing Treatment

Fabrication and characterization of in-situ TiAl matrix composite with controlled microlaminated architecture based on SiC/Al and Ti system

Influence of Raw Material Selection and Fabrication Parameters on Microstructure and Properties of Micro-Laminated TiB2–TiAl Composite Sheets

The Microstructure Evolution of TC4-(TiB + TiC)/TC4 Laminated Composites by Laser Melting Deposition

Synthesis and Mechanical Properties of Innovative (Tib/ti)-Ti3al Micro-Laminated Composites

Fabrication, Microstructure, and Mechanical Property of NiAl-based Composite with Microlaminated Architecture by Roll Bonding and Annealing Treatment

Microstructural Evolution in Cold-Rolled Squeeze-Cast Sicw/Al Composites During Annealing

Synthesis and Microstructural Characterization of Ti–Al3Ti Metal–intermetallic Laminate (MIL) Composites

The Effect of Annealing Temperature on Micro-Structure and Mechanical Properties of C/Sic Composites

Processing and mechanical behavior of laminated titanium–titanium tri-aluminide (Ti–Al3Ti) composites