Abstract:Novel ternary organic-inorganic composite nanofibrous mats are successfully prepared by cooperative fabrication via electrospinning. Poly(vinyl alcohol) (PVA) and poly(acrylic acid) (PAA) were chosen as the polymer components, while tetraethyl orthosilicate (TEOS) was used as the silicon source. By adjusting the mass ratio of polymer and silica gel, the obtained nanofibers with a mass ratio of 1 : 0.75 exhibit very uniform morphology with an average diameter of 845 nm. Systematic investigations were performed to illustrate the reaction process and internal structure of the nanofibers. The esterification and dehydration between PVA, PAA and hydrolytic TEOS are proposed to form an integrated network structure which makes the ternary electrospun nanofibrous mats more stable compared to pure single polymer and the binary composites. Eight typical solvent (H2O, DMF, EtOH, THF, MeOH, CHCl3, n-hexane and acetone) immersion experiments of the nanofibrous mats at varied temperatures (60, 80, 100, 120, 150 and 200 degrees C) were performed for the study of its solvent and thermal stability. The results show that the prepared ternary organic-inorganic nanofibrous mats exhibit remarkable solvent and temperature resistance (e. g. in DMF at 200 degrees C). Moreover, the obtained PVA/PAA/SiO2 nanofibrous mats also present desirable mechanical properties such as malleability with a high breaking elongation. Taking account of the availability of raw materials, easy maneuverability, and the outstanding chemical stability and mechanical properties, such a cooperative fabrication strategy could find great extensibility for the synthesis and application of multiple organic-inorganic composite materials.

Storage Stability And Mechanism Of Polyvinyl Pyrrolidone Based Alkoxide Composite Electrospun Fibres

Fabrication of Polyvinylpyrrolidone/Boehmite Nanofibers by Electrospinning

Dielectric Properties Of Electrospun Titanium Compound/Polymer Composite Nanofibres

Electrospinning Fabrication and Characterization of Poly(Vinyl Alcohol)/Layered Double Hydroxides Composite Fibers

Electrospun Polyvinyl Alcohol/Halloysite Nanotubes Composite Nanofibers

Composite Nanofibers for Textile Applications

Cooperative fabrication of ternary nanofibers with remarkable solvent and temperature resistance by electrospinning

Synthesis using electrospinning and stabilization of single layer macroporous films and fibrous networks of poly(vinyl alcohol)

Synthesis of Hollow PVP/Ag Nanoparticle Composite Fibers via Electrospinning under a Dense CO2 Environment

Fabrication and Characterisation of Titanium Dioxide (Tio2)/PVA Nanofibre Composites using Electrospinning

Preparation of Silica-Sustained Electrospun Polyvinylpyrrolidone Fibers with Uniform Mesopores Via Oxidative Removal of Template Molecules by H2o2 Treatment

Molecular Architecture and Enhanced Thermal Stability of Electrospun Poly(Epsilon-Caprolactone)/Aminopropyl Isobutyl Polyhedral Oligomeric Silsesquioxane Hybrid Fibers

Preparation and Characterization of Poly(vinyl Pyrrolidone)/fe3o4 Composite Nanofibers

Fabrication of luminescent hybrid fibres based on the encapsulation of polyoxometalate into polymer matrices

Flexible Polyethylene Glycol/polyvinylpyrrolidone Composite Phase Change Fibres: Preparation, Characterization, and Thermal Conductivity Enhancement

Electrospun Polyvinyl Alcohol/waterborne Polyurethane Composite Nanofibers Involving Cellulose Nanofibers

Preparation of Y3Al5O12 nanofibres by electrospinning

FABRICATION OF YTTRIUM ALUMINUM GARNET NANOFIBERS BY AN ELECTROSPINNING TECHNIQUE

Preparation and Characterization of Alginate/Polyvinyl Alcohol Composite Fibers Containing Copper Ions

Effect of polymer concentration and annealing temperature on TiO2-PVP composite nanofiber mats prepared with homemade electrospinning

Preparation and characterization of polyvinyl alcohol/sodium alginate/Pyrovatex CP composite fibers