Experimental and numerical study of Cu-SSZ-13 SCR system for NOx reduction and hydrothermal aging under diesel exhaust conditions
Yu Sun,Yejian Qian,Zhen Gong,Xiang Gu,Zhaohui Xie,Shun Meng,Binbin Tang
DOI: https://doi.org/10.1016/j.fuel.2023.129617
IF: 7.4
2023-08-30
Fuel
Abstract:Selective catalytic reduction (SCR) is a crucial technique for mitigating nitrogen oxides emission of internal combustion engines. Compared with vanadium-based catalysts, copper-based molecular sieve catalysts exhibit superior low-temperature catalytic performance and anti-aging properties. The catalytic characteristics of Cu-SSZ-13 catalyst in both fresh and aged states are investigated through experimental and numerical simulations. The catalytic performance of Cu-SSZ-13 catalyst with 200 g/L coating is investigated under wide inlet temperatures (180 °C–450 °C) and ANR (ammonia to nitrogen ratio) (1–1.4) conditions via an engine emission test device. Further, the apparatus is adopted to evaluate performance at various aging temperatures (600 °C, 700 °C, and 800 °C). The aging factor is introduced based on experimental results to establish and correct the kinetic model for SCR aging state. The results illuminate that the increase of ANR fails to compensate for decline of catalytic efficiency under low-temperature conditions (150 °C).The generated quantity of isocyanate acid through the side reaction of urea hydrolysis increases proportionally with ANR. And it increased supply only resulted in a marginal 1 %–3 % improvement of catalytic efficiency. As SV decreases from 60,000 h −1 to 35,000 h −1 , the catalyst efficiency increases from 22 % to 45 %, resulting in an elevation of reactant concentration and its gradient on the catalyst surface. This leads to accelerated reaction rates and enhanced diffusion effects. The catalytic efficiency can be significantly enhanced at low temperatures when NO 2 fraction in NOx falls within the range of 10 %–25 %. The sensitivity of SCR reactions to aging varies at low temperatures (<250 °C) due to the distinct reaction sites on catalyst for different types of SCR reactions. The NO 2 SCR reactions exhibit minimal susceptibility, while the rapid SCR reactions are significantly impeded. Moreover, it has been observed that the catalyst microstructure was completely deteriorated under hydrothermal aging test at 900 °C operating condition. In general, the low-temperature catalytic performance of Cu-SSZ-13 catalyst can be further optimized by pretreating inlet gas components and optimizing the catalyst structure.
energy & fuels,engineering, chemical