Abstract:Hydroxyapatite (HAp) and β-tricalcium phosphate (β-TCP) are widely used in bone graft materials, because they have excellent biocompatibility. However, the degradation rates of HAp and β-TCP do not match the rate of osteogenesis, which limits their clinical applications. Therefore, forming biphasic calcium phosphate (BCP) is a promising method to control the biodegradation rate of the material. In addition, strontium (Sr) is an important element that promotes osteogenesis and inhibits bone absorption. Therefore, this study focused on the effects of Sr in the as-synthesized BCP with varied Sr concentrations of 1, 5, and 15 mol%, which are synthesized by chemical precipitation and a high-temperature calcination method. In this study, we assume that Sr is doped into Ca(5) of β-TCP and Ca(1) & Ca(2) of HAp during the Rietveld refinement. On the basis of the Rietveld refinement results obtained from X-ray diffraction (XRD) patterns, with increasing Sr concentration, the mass percentage of HAp decreases first, which is due to the distortion of the HAp structure, resulting in a decrease in HAp stability and phase variation from HAp to β-TCP. However, when the concentration of Sr reaches 15 mol%, the mass percentage of HAp increases, which may be because of the phase transformation from β-TCP to calcium-deficient apatite by the diffusion of Ca. In addition, the increase in the lattice constants and volumes indicates that Sr has been successfully doped into the crystal lattices of both β-TCP and HAp, since the ion radius of Sr2+ (0.113 nm) is larger than the ion radius of Ca2+ (0.099 nm). As shown in the X-ray photoelectron spectroscopy (XPS) results, the intensities of Sr3d and Sr3p increase with increasing Sr concentrations, which indicates that Sr is not only on the surface of the sample but also in the crystalline structures of both β-TCP and HAp.

Preparation of Strontium-Barium Hydroxyapatite by Coprecipitation

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS112-b-PAA38

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS<sub>112</sub>-b-PAA<sub>38</sub>

Hydrothermal synthesis of nano-hydroxyapatite crystals

Preparation and Characterization of Strontium-Containing Hydroxyapatite Bone Cements

Wet synthesis and structure stability of strontium-containing hydroxyapatite

Influences of strontium on the phase composition and lattice structure of biphasic calcium phosphate

Preparation and Injectability of Strontium-Containing Hydroxyapatite Bone Cements

Preparation and characterization of carbonated barium-calcium hydroxyapatite solid solutions

Development of a Strontium-Containing Hydroxyapatite Bone Cement

Hydrothermal Preparation and Characterization of Ultralong Strontium-Substituted Hydroxyapatite Whiskers Using Acetamide As Homogeneous Precipitation Reagent.

Cathodic Synthesis of Strontium-Substituted Hydroxyapatite Coatings

Structural, mechanical and thermal features of Bi and Sr co-substituted hydroxyapatite

Preparation and Characterization of a New Type of Sr-Contained Hydroxyapatite Bone Cement

Low temperature preparation of strontium barium niobate powders from metal carboxylate gels

Thermal Stability of Nonstoichiometric Stronium-Incorporated Hydroxyapatite Synthesized with A Hydration Process

Preparation and thermal stability analysis of hydroxyapatite derived from the precipitation process and microwave irradiation method

Preparation of Pt-doped hydroxyapatite via wet co-precipitation method

Synthesis and characterization of pure and Mg, Cu, Ag, and Sr doped calcium-deficient hydroxyapatite from brushite as precursor using the dissolution-precipitation method

Characterization and Mineralization of Strontium Doped Nano Hydroxyapatite Coating on Titanium Rods

Structural Characterization of Low-Sr-Doped Hydroxyapatite Obtained by Solid-State Synthesis