Preparation and Characterization of Strontium-Containing Hydroxyapatite Bone Cements

Fu Yuanfei,Sun Zhaoyao,Chen Demin

2014-01-01

Rare Metal Materials and Engineering

Abstract:The powder of different strontium-containing (0at%, 5at%, 10at%, 15at% and 20at%) hydroxyapatite bone cements were synthesized from strontium carbonate, calcium carbonate and calcium phosphate dibasic by solid reaction. A mixed solutions that consisted of copolymer of acrylic acid/itaconic acid and citric acid were used for setting liquids. The structure of phases for 5 groups were determined by XRD and FT-IR. The setting time and compression strength of bone cements were determined according to the national pharmaceutical industry standard. The experiment results show that the structure of phases for sample groups of 0 at%, 5at%, 10at%, 15at% strontium amount were a series of strontium-containing alpha-TCP/HA biphases cement by the analyses of XRD and FTIR, but that of sample group of 20at% was strontium-containing beta-TCP/HA biphase. The FT-IR results are consistent with the XRD analysis. The setting time of 0at% similar to 15at% of strontium content sample group remained in the range of 6.5 7.5 min. While the 20at% of strontium content of sample group is not the formation of solidified body, even after 4 h the concoction was still in initial state of blending, illustrateing no hydration solidification. The 4 sample groups of compression strength of strontium content of 0, 5 at%, 10 at% and 15 at% were 61.8 15.2, 70.7 +/- 12.8, 73.4 +/- 15.5 and 68.3 +/- 18.1 MPa, respectively.