Abstract:Binary TiAl (Ti29.8Al and Ti33.3Al, weight percent, hereafter in wt.%) alloys with different SiC fibers contents were prepared by arc melting. Microstructure, phase transformation, mechanical properties and related mechanism were elaborately researched. For the microstructure of Ti29.8Al alloy, the matrix consisted of fully alpha(2)/gamma lamellar colonies, the grain morphology changed from columnar to equiaxed when the SiC content reached 0.9%. For Ti33.3Al alloy, the matrix consisted of alpha(2)/gamma lamellar colonies and gamma phases, the columnar grains changed to equiaxed grains when the SiC content was more than 0.3%, and the grain size decreased from 150.9 to 69.3 pm with increasing SiC content. Ti5Si3 phases formed at the grain boundaries of both SiC-containing binary alloys. Ti2AlC particles would appear in the lamellar colonies when the SiC content was more than 0.9% in Ti29.8Al alloy and 0.3% in Ti33.3A1 alloy, respectively. The formation of Ti5Si3 and Ti2AlC phases resulted from the reaction of SiC fibers and TiAl alloy. The solid solution of C element in alpha(2) phase is higher than that in gamma phase, Ti2AlC will be more easily formed in Ti33.3Al alloy due to less alpha(2) phases and more gamma phases comparing with Ti29.8Al alloy. Compressive testing results showed that the strength and the strain of SiC-containing Ti29.8Al alloy were almost unchanged until the SiC content was 0.9%, which were improved to 1383 MPa and 6.5%, respectively. A good combination of strength and ductility of SiC-containing Ti33.3Al alloy was obtained, the highest values of them were 2196 MPa and 27.5% when the SiC content was 0.5%. Improvement of mechanical properties is caused by the grain refinement, grain boundary strengthening of Ti5Si3 particles, load transfer strengthening of Ti2AlC particles and solid solution strengthening of C and Si atoms.

Study of Matrix Microstructure of SiCf/Ti–43Al–9V Composites

Microstructure inheritance of matrixes of SiCf/Ti6242 composites from precursor wire coatings by α+β phase field consolidation

Matrix microstructure evolution during the fabrication of SiCf/Ti60 composites

Microstructure and Interfacial Strength of SiC Fiber-Reinforced Ti17 Alloy Composites with Different Consolidation Temperatures

Microstructure Evolution of Interface and Matrix During the Preparation of SiCf/Ti60 Composites

Microstructure evolution of SiC whisker-reinforced Ti6Al4V matrix composites manufactured by selective laser melting during heat treatment

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

Microstructure and Compressive Properties Ofin SituSynthesized TiC/Ti Composites

Microstructure and compressive properties of in situ synthesized (TiB + TiC)/Ti composites

Microstructure Characterization of Al Matrix Composite Reinforced with Ti–6Al–4V Meshes after Compression by Scanning Electron Microscope and Transmission Electron Microscope

Microstructure characterization of Al matrix composite reinforced with Ti-6Al-4V meshes after compression by scanning electron microscope and transmission electron microscope.

Microstructure and Properties of C-f Reinforced Ti/Al Based Laminated Composites

Microstructure and mechanical properties of unidirectional W filament reinforced Al-6Ti-6Nb and SiCp-Al-6Ti-6Nb matrix composites

The Effect of Modulated Matrix Microstructure on the Deformation Behavior in SiCf/Ti17 Composites

Effects of Ti3SiC2 on microstructure and properties of TiC0.4 enhanced TiAl matrix composites

The microstructure and tensile properties of the Ti 2 AlC reinforced TiAl composites fabricated by powder metallurgy

Microstructure and mechanical properties of short-carbon-fiber/Ti3SiC2 composites

Preparation, Microstructure and Mechanical Properties of In-Situ TiC/Al–Si–Fe Aluminum Matrix Composites

Microstructure Evolution and Mechanical Properties of TiAl Binary Alloys Added with SiC Fibers

Microstructure of SiC<SUB>w</SUB> reinforced Al–12Ti composites prepared by powder metallurgical technique

Strengthening Effects of Tic Particles and Microstructure Refinement in in Situ Tic-Reinforced Ti Matrix Composites