Abstract:Novel red long-lasting phosphorescent materials beta-Zn-3(PO4)(2): Mn2+, M3+ (M = Al and Ga) were synthesized by means of high-temperature solid-state reaction. Photoluminescence (PL) excitation and emission, long-lasting phosphorescent (LLP) emission, decay curves, brightness and chromaticity coordination, and thermostimulated-luminescent (TSL) spectra were used to characterize the powder phosphors. The emissions for both PL and LLP are due to the T-4(1g)((4)G) --> (6)A(1g)(S-6) transition of Mn2+ ions in beta-Zn-3(PO4)(2). The incorporation of trivalent ions M 31 decreases the PL intensity and contrarily improves the LLP properties including brightness and duration with increasing ionic radius. After irradiation with ultraviolet light peaking at 254 nm, Zn-3(PO4)(2): Mn2+, Ga3+ shows the initial intensity of the red phosphorescence at 460 mcd m(-2) with the chromaticity coordinates x = 0.6679, y = 0.3321 after the removal of the excitation source. Its red phosphorescence lasts no less than 2.5 h. The results of TSL show that some intrinsic defects associated with peaks at 381, 450 and 510 K appear in Zn-3(PO4)(2): Mn2+ whereas a novel compensating defect V-Zn" for the substitution of Zn2+ by Al3+ and Ga3+ is associated with peaks at 380 K for Zn-3(PO4)(2): Mn2+, Al3+ and 377 K for Zn-3(PO4)(2): Mn2+, Ga3+. The negative defect V-Zn" serves as an efficient hole-trapping center. The density of the trapped-charges for the TSL peaks at 380 and 377 K is respectively 1.2 and 2.7 times more intensive than that for the peak at 381 K. The TSL intensity is strongly dependent on the density of the trapped charges. An electron - hole recombination model is proposed to interpret the mechanism for the red LLP of Mn2+. Based on this model, the improvement of red LLP performance of Mn2+ is strongly related to the density of the trapped charges, which can be modified by the added ions. It demonstrates that the red LLP performance of Mn2+ can be controlled by the species of the auxiliary ions.

Photoluminescence Properties of a New Red-Emitting Mn-activated ZnGa2S4 Phosphor

Photoluminescence properties of new deep red-emitting Mn 2+ -activated CaLaGa 3 S 6 O phosphors

Preparation, Structural and Photoluminescence Characteristics of Novel Red Emitting Mg7ga2geo12:Mn4+ Phosphor

Structure and Photoluminescence Properties of Rare-Earth Free Narrow-Band Red-Emitting Mg6zngega2o12: Mn4+ Phosphor Excited by Nuv Light

Monodisperse Micro-Spherical Sr2–Mg1+Y Al22–O36:xMn4+ Red Phosphors

Photoluminescence Properties of Zn0.9Mg0.1S Phosphors Doped by Europium and Manganese Ions

Insight into a Novel Rare-Earth-free Red-Emitting Phosphor Li3Mg2NbO6:Mn4+: Structure and Luminescence Properties

A new deep red-emitting Mn2+-activated SrLaGa3S 6O phosphor

Synthesis, Photoluminescence and Thermostimulated-Luminescence Properties of Novel Red Long-Lasting Phosphorescent Materials Β-Zn3(po4)2:Mn2+,m3+(m = Al and Ga)

Preparation and photoluminescence study of rare-earth-free red emitting La[math]Ga[math]SiO[math]:Mn[math]phosphors

Broadly tunable emission from Mn-doped zinc gallogermanate phosphors through composition modification

A Novel Red-Emitting Mn-activated BaZnOS Phosphor

Enhancement UV and VUV Photoluminescence of Zn2SiO4:Mn2+ with the Incorporation of Ga3+

A strong zero phonon line of Mn4+ in a red-emitting phosphor BaGaF5:Mn4+

Photoluminescence Properties Of A Novel Red Fluoride K2ligaf6: Mn4+ Nanophosphor

Deep-red-emitting Mg2InSbO6:Mn4+ Phosphors with a Double-Perovskite Structure for Plant-Cultivation LEDs: Synthesis and Photoluminescence Properties

Room-temperature synthesis, controllable morphology and optical characteristics of narrow-band red phosphor K2LiGaF6:Mn4+

A New Deep Red-Emitting Mn<sup>2+</sup>-Activated SrLaGa<sub>3</sub>S<sub>6</sub>O Phosphor

Synthesis and characterization of Zn 2 GeO 4 :Mn 2+ phosphor for field emission displays

Synthesis and Luminescence Properties of Red Phosphors: Mn2+ Doped MgSiO3 and Mg2SiO4 Prepared by Sol-Gel Method

Intense Red Photoluminescence from Mn2+-doped (na+; Zn2+) Sulfophosphate Glasses and Glass Ceramics As LED Converters.