Abstract:Vinyl MQ silicone resin (M and Q respectively represent R3SiO1/2 and SiO4/2) was synthesized via the hydrolytic condensation of hexamethyldisiloxane, 1, 3-divinyl-1, 1, 3, 3-tetramethyldisiloxane and tetraethyl orthosi-licate, and the effects of polymerization conditions on the properties of the product were investigated. Then, a series of room-temperature vulcanizing (RTV) silicone rubbers reinforced with vinyl MQ silicone resin were prepared from vinylterminated polydimethylsiloxane (PVMS) cured with organohydrogenpolysiloxane under the catalysis of Pt catalyst. Finally, the effects of the preparation process on the mechanical properties and transparency of the cured silicone rubbers were investigated. The results show that the synthesized MQ silicone resin is of the best reinforcement effect when HCl and ethanol contents are respectively 4.0% and 1.6% and when the M/Q molar ratio is 0.75, and that, when the mass ratio of PVMS to MQ silicone resin is 1, the molar ratio of Si-H to Si-Vi is 1.4, the catalyst dosage is 10 μg/g and the inhibitor dosage is 0.3 mg/g, the cured silicone rubbers are of a tensile strength being up to 7.2 MPa and of excellent transparency owing to the reinforcement of MQ silicone resin.

Effects of Preparation Process of MQ Silicone Resin on Reinforcement of RTV Silicone Rubber