Significance of retained austenite stability on yield point elongation phenomenon in a hot‐rolled and intercritically annealed medium‐Mn steel
Ying Dong,Min Qi,Yu Du,Hongyan Wu,Xiuhua Gao,Linxiu Du,Y. Dong,M. Qi,Y. Du,H.Y. Wu,X.H. Gao,L.X. Du
DOI: https://doi.org/10.1002/srin.202200400
IF: 2.1258
2022-08-17
steel research international
Abstract:We elucidate here the effect of retained austenite stability on yield point elongation (YPE) phenomenon in a hot‐rolled and intercritically annealed medium‐Mn steel. Furthermore, the influencing factors of austenite reversion were studied. The results indicated that the shear phase transition was suppressed by the strain hardening of prior austenite grain (PAG) introduced by low‐temperature rolling, resulting in the refined martensite laths with high dislocation density. The nucleation and growth of intercritical austenite was accelerated by high density dislocation substructures. Different characteristics of retained austenite (RA) were obtained through tailoring the rolling temperature and austenite reversion transformation (ART) process. YPE phenomenon is a result of the equilibrium between work hardening (via martensitic transformation and dislocation multiplication) and softening (by stress relaxation and dislocation glide). In the initial deformation stage, large amounts of geometrically necessary dislocations (GND) were 'stored' in the RA with higher stability, and the local stress can be effectively relaxed and transferred, leading to the occurrence of YPE. The optimum properties were obtained in R760‐A630‐0.3h samples with combination of yield strength of 918 MPa, tensile strength of 1019 MPa and total elongation of 25.3%, which was mainly attributed to the finer ferrite matrix and sustained TRIP effect. This article is protected by copyright. All rights reserved.
metallurgy & metallurgical engineering