Study of dynamic and permanent indentation of laminates subjected to low-velocity impact
Debo Liu,Zhidong Guan,Wei He,Jun Wang
2011-01-01
Abstract:Composite materials are now being used in primary aircraft structures, particularly in helicopters, light aircrafts, commercial planes and sailplanes, because of their numerous advantages including low weight, high modulus and strengths and the possibility of manufacturing large integral shell structures. However, a well-known problem with composite laminates is their poor resistance to accidental impact by foreign objects. The resulting damage due to impacts, often in the form of delamination, matrix cracking and fiber failures, may severely reduce the structural strength and stability[1]. Therefore, considerable amount of research has been done in the area of impact of composite structures. The relationship between the indentation and impact energy has been studied by many investigators[2]. It is proved to be an effective method to evaluate the internal damage by observing the indentation. Laminated composite panels with BVID (Barely Visible Impact Damage) are required to endure the full DUL (Design Ultimate Load) in the strength criteria usually adopted in composite wing structure design in civil aviation. BVID primarily considers the depth of the permanent indentation. More exactly the depth of indentation after impact is measured, more accurate evaluation of composite can be made, which provides a reference to the design of composite structure. With the development of computer, many calculative methods were raised to study the formation of the indentation, which made it possible to gain an insight into the damage theory of composites. In the simulation of the impact, Hertzian contact law has been widely used to calculate the contact force between the impactor and the laminates. In 1977, C.T. Sun proposed a modified Hertzian contact law [3]. In 1981, Yang and Sun experimentally investigated indentation phenomena through static indentation tests on composite laminated specimens and they presented the experimental static indentation law[4]. In order to follow the approach, researchers needed to develop their own finite element method (FEM) program. Many new damage theories and analytical methods were established to simulate the damage evolution process during the impact. At present, the dynamic process of the indentation growth has been studied a lot by the simulation but rarely by experiment, because it was impossible to observe the details between the impactor and the laminates during impact test. Most contact laws are based on Hertzian/modified Hertzian contact law, which was generalized from the static indentation test. It is necessary to measure the dynamic changes of the indentation during the impact test to understand the damage evolution process better. In the present study, firstly, a simplified method was introduced to measure the thickness changes of the laminates at the impact point during the experiment. Secondly, a modified Hertzian contact law was raised based on the dynamic indentation. Thirdly, a calculative method was developed to predict the permanent indentation.