Evolution of Phase Transformation Behavior and Dielectric Temperature Stability of BaTiO3–Bi(Zn0.5Zr0.5)O3 Ceramics System

Yiliang Wang,Xiuli Chen,Huanfu Zhou,Liang Fang,Laijun Liu,Hui Zhang

DOI: https://doi.org/10.1016/j.jallcom.2012.09.127

IF: 6.2

2013-01-01

Journal of Alloys and Compounds

Abstract:(1−x)BaTiO3–xBi(Zn0.5Zr0.5)O3 [(1−x)BT–xBZZ, 0.01⩽x⩽0.6] ceramics were synthesized by solid-state reaction technique. Based on the X-ray diffraction data analysis, a systematic structure change from the ferroelectric tetragonal phase to pseudocubic phase and the pseudocubic phase to orthorhombic phase was observed near x=0.07 and x=0.4 at room temperature, respectively. Dielectric measurements show a dielectric anomaly, over the temperature range from 50 to 200°C for the compositions with 0.03⩽x⩽0.09. A change from a normal ferroelectric behavior to diffusive and dispersive relaxor-like characteristic was also observed. Moreover, (1−x)BT–xBZZ ceramics show good dielectric temperature stability over a wide temperature range, which indicates that these ceramics can be applied in the temperature stability devices.