Abstract:The augmented finite element method (A-FEM) is used to study the fundamental composite failure problem of delamination and associated damage events spreading from a stress concentrator during tensile loading. The solution exploits the ability of A-FEM to account for coupled multiple crack types that are not predetermined in shape or number. The nonlinear processes of each fracture mode are represented by a cohesive model, which provides a unified description of crack initiation and propagation and can also describe crack coalescence and bifurcation. The study problem is an orthogonal double-notched tension specimen, in which delaminations interact with transverse ply cracks, intra-ply splitting cracks, non-localized fine-scale matrix shear deformation, and fiber breaks. Cohesive laws and constitutive laws for matrix shear deformation are calibrated using literature data from independent tests. The calibrated simulations are mesh independent and correctly reproduce all qualitative aspects of the coupled damage evolution processes. They also correctly predict delamination sizes and shapes, the density of transverse ply cracks, the growth rate of splitting cracks, softening of the global stress–strain curve, and the ultimate strength. A sensitivity analysis relates variability in cohesive law parameters to predicted deviance in engineering properties. Given the known variability in cohesive law parameters, the predicted deviance in ultimate strength agrees with that in experimental data. The importance of including the interactions between different crack systems and non-localized shear deformation is demonstrated by suppressing the presence of separate mechanisms; the predicted delamination shapes, splitting crack growth rate, and the stress–displacement relationship fall into significant error.

Finite Element Simulation of the Failure Process of Single Fiber Composites Considering Interface Properties

Micro Failure Analysis of Fiber Metal Laminates

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Progressive failure analysis of 2D woven composites at the meso-micro scale

Numerical Simulation of the Fiber Fragmentation Process in Single-Fiber Composites

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension

Finite Element Analysis of Progressive Failure and Strain Localization of Carbon Fiber/Epoxy Composite Laminates by ABAQUS

A Monte Carlo finite element simulation of damage and failure in SiC/Ti–Al composites

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

Numerical Simulation of Low Velocity Impact Failure of CCF300 Carbon Fiber Laminate Based on ABAQUS

A Monte Carlo simulation of damage and failure process with crack saturation for unidirectional fiber reinforced ceramic composites

Comprehensive inter-fibre failure analysis and failure criteria comparison for composite materials using micromechanical modelling under biaxial loading

Phase field modeling for composite material failure

An efficient micromechanics-based finite element model for failure analysis of laminated composites

A Numerical Method for Simulating the Microscopic Damage Evolution in Composites under Uniaxial Transverse Tension

A novel phase‐field based cohesive zone model for modeling interfacial failure in composites

Damage failure mechanism of unidirectional fiber reinforced SiC f /SiC composites under uniaxial tension

A 3D Cohesive‐frictional Coupled Interface Model for Mesoscale Simulation of Steel Fibre‐reinforced Concrete

Micromechanical modeling of longitudinal compression behavior and failure mechanism of unidirectional carbon fiber reinforced aluminum composites involving initial fiber misalignment