Size Effect on Hydrogen Storage Properties of NaAlH4 Confined in Uniform Porous Carbons

Xiulin Fan,Xuezhang Xiao,Jie Shao,Liuting Zhang,Shouquan Li,Hongwei Ge,Qidong Wang,Lixin Chen

DOI: https://doi.org/10.1016/j.nanoen.2013.03.021

IF: 17.6

2013-01-01

Nano Energy

Abstract:Uniform porous carbons with pore size of 200nm, 60nm, 30nm and 4nm were separately synthesized using hard-template method, and nanoparticles of NaAlH4 have been infiltrated into the above porous carbons. A correlation between pore size and hydrogen desorption kinetics of NaAlH4 is established. In contrast with bulk NaAlH4, all of the confined NaAlH4 exhibit a single-step dehydrogenation process to form NaH/Al product. However, the onset and peak hydrogen desorption temperatures are significantly influenced by the pore size of carbon. As the pore size is reduced to 30nm, NaAlH4 starts to decompose at temperature of about 100°C, with a dehydrogenation peak of 172°C. The apparent activation energy for dehydrogenation is estimated to be 84.9 and 69.7kJ/mol for the NaAlH4 confined in 30 and 4nm porous carbons, reduced by 43 and 58kJ/mol contrast to the first step of bulk NaAlH4, respectively. Besides, by confining NaAlH4 into porous carbon with pore size≤30nm, the in situ generated NaH can decompose at a temperature below 250°C, i.e. reduction of the temperature for 100°C compared with that generated by decomposition of bulk NaAlH4. Thus all of hydrogen in NaAlH4 can be released and utilized at a relatively moderate condition without doping additives. Cycling investigation shows that smaller size exerts a favorable effect on the hydrogen storage capacity retention.