Microstructure and optical property of MgAl2O4 transparent ceramics

付萍,许永,吕文中,雷文

DOI: https://doi.org/10.13245/j.hust.2013.10.007

2013-01-01

Abstract:MgAl2O4 transparent ceramics were fabricated through a high-temperature calcinated nanosized MgAl2O4 powders by spark plasma sintering (SPS). Various SPS parameters were studied systematically to investigate the effect of the parameters on the densification, grain size and optical property of MgAl2O4 transparent ceramics. The microstructure and optical properties were characterized by scan electronic microscope (SEM), ultraviolet-visible spectroscopy (UV-Vis) and Fourier transform infrared spectroscopy (FT-IR). The experimental results indicate that the residual porosity, pore size and grain size distribution of transparent ceramics change with SPS parameters influenced by the optical properties considerably. The in-line transmittance of the dense sintered ceramics with an average grain size of 200 nm can be as high as 66% at 550 nm and 80% at 2000 nm by spark plasma sintering at 1325°C for 15 min with the heating rate of 13°C/min at pressure 70 MPa loaded at 1100°C.