Abstract:Ordered mesoporous carbon (OMC)-metal oxide composites have attracted great interest due to their combination of high surface area, uniform pores, good conductivity of mesoporous carbon, and excellent photo-, electro- and chemical sensing properties of metal oxides. Herein, OMC-metal oxide composites with large mesopores and monodispersed CoOx nanoparticles were synthesized via a controllable multicomponent cooperative coassembly of ultra-high-molecular-weight poly(ethylene oxide)-block-polystyrene (PEO-b-PS) copolymers, resol (soluble phenoic resin carbon precursor), and cobalt nitrate (cobalt oxide precursor). The obtained nanocomposites possess a face-centered cubic (fcc) mesoporous structure, large pore size (13.4-16.0 nm), high surface area (394-483 m(2)/g), large pore volume (0.41-0.48 cm(3)/g), and uniform CoOx nanoparticles with tunable diameters (6.4-16.7 nm). The long chain length of amphiphilic PEO-b-PS template molecules contributes to large mesopores and thick pore walls that allow a controllable nucleation of metal oxides and the formation of CoOx nanoparticles that are partially embedded and stabilized in the graphitic carbon walls and semiexposed in the mesopore channels, avoiding pore blockage and facilitating the mass transportation of guest molecules. The in situ loaded highly dispersed CoOx nanoparticles promote the graphitization of carbon frameworks during the pyrolysis procedure at relative lower temperatures (similar to 700 degrees C). Due to the strong synergistic effect between the graphitic OMC with large pores and uniform active p-type CoOx nanoparticles, the obtained mesoporous nanocomposite exhibit superior performance in hydrogen sensing.

Synthesis and Electrochemical Characterization of N-Doped Partially Graphitized Ordered Mesoporous Carbon–Co Composite

Co-modified Ni/N-doped Carbon As Electrocatalysts for HER and OER

Performance of Nitrogen-Containing Macroporous Carbon Supported Cobalt Catalyst Synthesized Through In-Situ Construction of Catalytic Sites for Oxygen Reduction Reaction

Controlled Synthesis of Ordered Mesoporous Carbon-Cobalt Oxide Nanocomposites with Large Mesopores and Graphitic Walls

Cobalt-nitrogen-doped Ordered Macro-/Mesoporous Carbon for Highly Efficient Oxygen Reduction Reaction

Co-MOF-derived core–shell CoP@Co3O4 nanoparticle loaded N-doped graphene: an efficient catalyst for the oxygen evolution reaction

Synergistic effects of N-doping and mesoporous structures in block copolymer-derived three-dimensionally ordered mesoporous carbon for PEMFC

Dicyandiamide-assisted synthesis of N-doped porous CoMn-Nx@N-C carbon nanotube composites via MOFs as efficient trifunctional electrocatalysts in the same electrolyte

ZIF-8/ZIF-67-Derived Co-N-x-Embedded 1D Porous Carbon Nanofibers with Graphitic Carbon-Encased Co Nanoparticles As an Efficient Bifunctional Electrocatalyst

N-doped graphitic carbon encapsulating cobalt nanoparticles derived from novel metal–organic frameworks for electrocatalytic oxygen evolution reaction

Ordered macroporous carbonous skeletons implanted with dual-phase Co/CoFe nanoparticles for boosting electrocatalytic performance

Co Nanoparticles Encapsulated in N-Doped Carbon Nanosheets: Enhancing Oxygen Reduction Catalysis Without Metal-Nitrogen Bonding.

Controllable synthesis of nitrogen-doped carbon containing Co and Co3Fe7 nanoparticles as effective catalysts for electrochemical oxygen conversion

In Situ Anchoring of Zeolite Imidazole Framework-Derived Co, N-Doped Porous Carbon on Multiwalled Carbon Nanotubes Toward Efficient Electrocatalytic Oxygen Reduction

A controllable synthesis of rich nitrogen-doped ordered mesoporous carbon for CO2 capture and supercapacitors

Enhanced N-doping in mesoporous carbon for efficient electrocatalytic CO 2 conversion

Mof Derived Carbon Encapsulation Coni Nanocrystal In-Situ Grafting of N-Doped Carbon Nanotubes for Synergistically Enhancing Electrocatalytic Active for Methanol Oxidation

Nitrogen‐Doped Nanoporous Graphenic Carbon: An Efficient Conducting Support for O

Iron, Cobalt, and Nitrogen Tri‐Doped Ordered Mesoporous Carbon As a Highly Efficient Electrocatalyst for Oxygen Reduction Reaction

N-doped carbon material encapsulated cobalt nanoparticles for bifunctional electrocatalysts derived from a porous Co(II)-based metal-organic frameworks (MOFs)

Hollow CoO Nanoparticles Embedded in N‐doped Mesoporous Graphene for Efficient Oxygen Reduction Reaction