Entropy-driven structural transition from tetragonal to cubic phase: High thermoelectric performance of CuCdInSe 3 compound
Tingting Luo,Yihao Hu,Shi Liu,Fanjie Xia,Junhao Qiu,Haoyang Peng,Keke Liu,Quansheng Guo,XingZhong Li,Dongwang Yang,Xianli Su,Jinsong Wu,Xinfeng Tang
DOI: https://doi.org/10.1016/j.mtphys.2023.101211
IF: 11.021
2023-08-24
Materials Today Physics
Abstract:Cu based chalcopyrite is an important class of thermoelectric materials with excellent electronic properties, however, the thermal conductivity is relatively high due to the simple tetragonal structure with highly ordered configuration on cation sites, limiting the thermoelectric performance . Herein, we realize that the modulation of entropy via alloying CdSe achieves the structural transition from tetragonal structure with ordered configuration on cations sites in CuInSe2 compound to cubic CuCdInSe3. CuCdInSe 3 crystallizes in a zinc blende (ZnS) structure where Cu, Cd and In cations randomly occupy the Zn site with the occupancy fraction 1/3. This entropy driven order-disorder transition on the cation site, in conjunction with the intensified point defect phonon scattering via alloying CdSe in CuInSe 2 , dramatically suppress the thermal conductivity. An ultra-low thermal conductivity of 0.76 Wm −1 K −1 at 780 K is achieved for CuCdInSe 3 compound, which is only about 2/3 in comparison with that of CuInSe 2 . CuCdInSe 3 is an indirect semiconductor, with the minimum of conduction band (CBM) located at Γ point and the maximum of valence band (VBM) between Γ and A. The density of states in VBM of CuCdInSe 3 are mainly contributed by the hybridization between Se-4p and Cu-3d orbitals, while that of CBM is dominant by Se-4p and In-5s orbitals. Minute adjustment of Cd content in CuCd (1+x) InSe 3 effectively modulates the carrier concentration and an optimized power factor of 0.58 Wm −1 K −2 is attained at 578 K for CuCd 1.01 InSe 3 , which is 9.6 times as high as the pristine CuCdInSe 3 . The improved electronic properties integrated with the intrinsically low thermal conductivity result in an enhanced thermoelectric figure-of-merit ZT value of 0.45 at 780 K for CuCd 1.005 InSe 3 , which is seven times higher than that of the pristine CuCdInSe 3 .
materials science, multidisciplinary,physics, applied