Crystallographic and Electrochemical Performances of La0.7ce0.3ni3.65co0.1mn0.35al0.15cu0.75-Xvx (X=0.05-0.20) Alloys

Xianyun Peng,Baozhong Liu,Yanping Fan,Liqiang Ji,Qian Li,Zhi Zhang

DOI: https://doi.org/10.1016/s1452-3981(23)14852-8

IF: 1.541

2013-01-01

International Journal of Electrochemical Science

Abstract:Microstructures and electrochemical properties of La0.7Ce0.3Ni3.65Co0.1Mn0.35Al0.15Cu0.75-xVx alloys are studied. X-ray diffraction results indicate that all alloys are identified with LaNi5 phase with CaCu5 type hexagonal structure. Calculated lattice parameter a, c and cell volume V increase, and a/c increases with increasing x value. Maximum discharge capacity of the alloy electrodes decreases from 322.9 mAh/g (x = 0.05) to 301.2 mAh/g (x = 0.20). High-rate dischargeability at the discharge current density of 1200 mA/g increases from 56.3% (x = 0.05) to 63.5% (x = 0.20). Cycling capacity retention rate at 100th cycles first increases from 69.9% (x = 0.05) to 72.3% (x = 0.10), and then decreases to 66.5% (x = 0.20), which should be ascribed to combined effect of advantageous and disadvantageous factors.