Improvement of the Electrochemical Performance of Carbon-Coated Lifepo4 Modified with Reduced Graphene Oxide

Bo Wang,Dianlong Wang,Qiuming Wang,Tiefeng Liu,Chenfeng Guo,Xiusong Zhao
DOI: https://doi.org/10.1039/c2ta00106c
IF: 11.9
2013-01-01
Journal of Materials Chemistry A
Abstract:In this work, carbon-coated LiFePO4 was further modified with reduced graphene oxide (RGO) using an ultrasonic-assisted rheological phase method coupled with carbothermal treatment. X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), and electrochemical methods were used to characterize the material's properties. The results showed that the composite material consisting of carbon-coated LiFePO4 and RGO sheets possesses a unique and effective three-dimensional “sheet-web” structure. In the structure, the LiFePO4 particle size can be maintained at nanosize to form abundant voids between the nanoparticles while the RGO sheets are significantly beneficial for Li+ diffusion. As a result, the electrochemical properties of the composite material have been greatly improved. A sample with 5 wt% RGO exhibited high specific capacity and superior rate performance with the discharge capacities of 160.4 mA h g−1 at 0.2 C and 115.0 mA h g−1 at 20 C. The sample also showed an excellent cycling stability with only about 10% capacity decay at 10 C after 1000 cycles.
What problem does this paper attempt to address?