Abstract:Herein the edge effect from the traction-free boundary condition is utilized to direct the spontaneous surface wrinkling. This boundary condition is attained by a simple combination of mechanical straining and selective exposure of polydimethylsiloxane (PDMS) substrate to O2 plasma (OP) through a copper grid. When the strained PDMS sheet is subjected to selective OP treatment, a patterned heterogeneous surface composed of the OP-exposed "hard" oxidized SiOx region (denoted as D1) and the OP-unexposed "soft" region (denoted as D2) is produced. The subsequent full release of the prestrain (ε(pre)) leads to the selective wrinkling in D1, rather than in D2. It is seen that even in D1, no wrinkling occurs in the vicinity of the D1 edge that is perpendicular to the wavevector. Furthermore, the average wrinkle wavelength in D1 (λ(D1)) is smaller than that of the exposed copper grid-free blank area (λ(blank)). This wavelength decrement between λ(D1) and λ(blank), which can be used to roughly estimate the edge-effect extent, increases with the applied mesh number of copper grids and exposure duration, while decreases with the increase of ε(pre). Meanwhile, there exists a decrease in the amplitude of the patterned wrinkles, when compared with that of the blank region. Additionally, hierarchical wrinkling is induced when the strain-free PDMS substrate is selectively exposed to OP, followed by uniaxial stretching and the subsequent blanket exposure. Consequently, oriented wrinkles perpendicular to the stretching direction are generated in D2. With respect to D1, no wrinkling happens or orthogonal wrinkles occur in this region depending on the applied mesh number, exposure duration, and ε(pre). In the above wrinkling process, the combinative edge effects in two perpendicular directions that are involved sequentially have been discussed.

Well-defined orthogonal surface wrinkles directed by the wrinkled boundary

Spatially Configuring Wrinkle Pattern and Multiscale Surface Evolution with Structural Confinement

Hierarchical Structures: Spatially Configuring Wrinkle Pattern and Multiscale Surface Evolution with Structural Confinement (adv. Funct. Mater. 1/2018)

Controlled Free Edge Effects in Surface Wrinkling Via Combination of External Straining and Selective O-2 Plasma Exposure

Unique Aspects of a Shape Memory Polymer As the Substrate for Surface Wrinkling.

Fabrication of Controlled Hierarchical Wrinkle Structures on Polydimethylsiloxane Via One-Step C4F8 Plasma Treatment

Harnessing Fold-to-wrinkle Transition and Hierarchical Wrinkling on Soft Material Surfaces by Regulating Substrate Stiffness and Sputtering Flux

Controlling and Prevention of Surface Wrinkling Via Size-Dependent Critical Wrinkling Strain.

Harnessing Heterogeneous Wrinkles in Metal/Polydimethylsiloxane Film System by Combination of Mechanical Loading and Heat Treatment

Surface Wrinkling Patterns of Film–Substrate Systems with a Structured Interface

Regulating Wrinkling Patterns by Periodic Surface Stiffness in Film-Substrate Structures

Curvature Induced Hierarchical Wrinkling Patterns in Soft Bilayers

Controlled Preparation of Highly Stretchable, Crack-Free Wrinkled Surfaces with Tunable Wetting and Optical Properties

Effect of Lateral Dimension on the Surface Wrinkling of a Thin Film on Compliant Substrate Induced by Differential Growth/swelling

Orientable Wrinkles in Stretched Orthotropic Films

Tunable Formation of Ordered Wrinkles in Metal Films with Controlled Thickness Gradients Deposited on Soft Elastic Substrates.

Surface Wrinkling with Memory for Programming Adhesion and Wettability

Photochemical Design for Diverse Controllable Patterns in Self-Wrinkling Films

Controlled Wrinkling Patterns in Periodic Thickness-Gradient Films on Polydimethylsiloxane Substrates

Surface effects on the wrinkles in a stiff thin film bonded to a compliant substrate

Regulating surface wrinkles using light