Abstract:The precursors of the hydrotalcite (HT) and the Co-containing hydrotalcite-like compounds (HTLcs) using coprecipitation method and the mixed oxides of 2Mg/Al, Co/Mg/Al, 1.5Co/0.5Mg/Al and 2Co/Al using calcination of the precursors were prepared. Various measured methods, such as BET, XRD, TG-DTA, TPR, FT-IR, microcalorimetric adsorption and isopropanol catalytic reaction were used to study the physico-chemical properties of these samples. The results showed that the specific surface areas of the mixed oxides derived from the HT and HTLcs precursors are larger whereas decreased with the increase of the Co content in the sample. After the cobalt cations were introduced into the HT structure, due to the redox properties of the cobalt cations, the binding abilities of the HT layers attracted the interlayer anions were weakened, which thence enabled that the thermal decomposition temperature and the thermostability were descended, and after calcination, which resulted in the specific surface areas of the Co-containing mixed oxides are lower than that of the 2Mg/Al sample. In TPR process, the 2Mg/Al sample is not reduced, while the reduction of the Co-containing mixed oxide is via a path of Co3+ to Co2+ and then to Co-0. The surface of the mixed oxide was showed to contain the acidic sites and the basic sites, and with the change of the Co content in sample the acidic sites and the basic sites were gained some adjustments. The FT-IR indicated that on the surface of the Co-containing mixed oxide the Lewis acid sites were the main and the Bronsted acid sites were the less. The acetone selectivity of the isopropanol catalytic reaction was the highest, which indicated that the redox surface sites on these samples were in the dominant position. Due to the addition of Co and the enhancement of the Co content in these samples, the conversion of the isopropanol catalytic reaction was increased also.

Citral-acetone condensation over catalysts prepared from C/MgAl hydrotalcite hybrids

Ce/MgAl mixed oxides derived from hydrotalcite LDH precursors as highly efficient catalysts for ketonization of carboxylic acid

Preparation, Characterization, and Catalytical Application of MgCoAl-Hydrotalcite-Like Compounds

Transesterification of Tributyrin with Methanol over MgAl Mixed Oxides Derived from MgAl Hydrotalcites Synthesized in the Presence of Glucose

Synthesis of methyl acetoacetate from acetone and dimethyl carbonate over Mg/Al mixed oxides

Catalytic Synthesis of Benzoin Methyl Ether on Magnesium-Cobalt-Aluminium Hydrotalcite-Like Compounds

Studies of the Mg-Al and Cation-Incorporated Hydrotalcites

Synthesis of acetals and ketals catalyzed by HMAS-5 molecular sieve

Study On Catalytic Synthesis Of 1,3-Benzodioxoles By Haimcm-41 Zeolite

Synthesis Of Mg-Zn-Al Hydrotalcites-Like And Catalytic Activities Of Their Composite Oxides

Transition Metal-Modified Mesoporous Mg-Al Mixed Oxides: Stable Base Catalysts for the Synthesis of Diethyl Carbonate from Ethyl Carbamate and Ethanol

Effect of coprecipitation method on Mg–Al hydrotalcite properties: application in the synthesis of diethylene glycol di-(methyl carbonate)

Synergistic Catalysis by MgO Induced Acid‐Base Bifunctional Sites for Cross Condensation of HCHO and Acetaldehyde

Aldol Condensation of Acetone over Mg–Al Mixed Oxides Catalyst Prepared by a Citric Acid Route

Isomerization Kinetics of Glucose to Fructose in Aqueous Solution with Magnesium‐Aluminum Hydrotalcites

Study on the Preparation,Characterization and Catalysis Performance of MgCoAl-HTLcs

Highly Selective Catalytic Oxidation of Glycerol by Cu-Containing Hydrotalcites

M−Mn−Al Hydrotalcite-like Compounds As Precursors for Methyl Benzoate Hydrogenation Catalysts

Synthesis, Characterization And Isopropanol Catalytic Reaction Of Mg/Al,Co/Al And Co/Mg/Al Mixed Oxides From Hydrotalcite And Hydrotalcite-Like Precursors

Structure-Activity Correlations of Lino3/Mg4alo5.5 Catalysts for Glycerol Carbonate Synthesis from Glycerol and Dimethyl Carbonate

Tailoring Catalytic Properties of CuMgAl Hydrotalcites for Selective Hydrogenolysis of Cellulose