Electrochemical Behavior Of Corrosion Resistance Of X65/Inconel 625 Welded Joints

L. Y. Xu,M. Li,H. Y. Jing,Y. D. Han
DOI: https://doi.org/10.1016/s1452-3981(23)14291-x
IF: 1.541
2013-01-01
International Journal of Electrochemical Science
Abstract:The corrosion resistant alloy of Inconel 625 is cladded on the inner surface of the carbon pipeline steels of X65. Two sections of the corrosion resistant alloy (X65/Inconel 625) were welded by tungsten inert gas welding (TIG) with adding material of ERCrNiMo-3. The electrochemical behavior of the weld metal, heat affected zone (HAZ) and base metal of clad pipe alloys (X65/Inconel 625) was investigated at ambient temperature in 3.5% NaCl solution using potentiodynamic polarization. To reveal the corrosion resistance of different regions in the corrosion resistant alloys welded joints, some significant characterization parameters such as E-corr, E-b, I-corr and Delta E in polarisation curves were analyzed and compared. The surface morphology of corrosion products was also analyzed by scanning electron microscopy (SEM) and energy-dispersive spectrometer (EDS). The results show that the corrosion resistance of the corrosion resistant alloys in 3.5% NaCl solution at ambient temperature follows the sequence: Root weld>Upper weld>Base metal>Lower HAZ>Upper HAZ.
What problem does this paper attempt to address?